Semiconductor device and its manufacturing method

ABSTRACT

The present invention relates to a semiconductor device in which a capacitance element is mounted on a semiconductor substrate as well as a method of fabricating the device. According to the present invention, a substantial lower electrode is formed on a semiconductor substrate through a first insulation film; a peripheral electrode, i.e. the periphery of the lower electrode or a dummy electrode, which has the surface higher than the surface of the lower electrode being formed integrally with or separately from the lower electrode; an upper electrode being formed on the lower electrode through a dielectric film; a capacitance element being formed so that at least the surface of the dielectric film may lie on a level lower than the surface of the peripheral electrode; and a recess surrounded by the peripheral electrode being filled with a smoothing film.  
     As a result, when the smoothing film is formed, at least the dielectric film does not sustain damage and so a capacitance element having less fluctuation in its characteristics and high reliability can be obtained.

DESCRIPTION OF REFERENCE NUMERALS

[0001]10 . . . Semiconductor Substrate

[0002]12 . . . The First Insulation Film

[0003]14 . . . Polysilicon Dummy Layer

[0004]16 . . . The Second Insulation Film

[0005]18 . . . TiN/Al-Si/Ti/TiON/Ti Lamination film

[0006]18 a, 18 b, 18 d . . . Lower Electrode

[0007]18 c . . . Dummy Electrode

[0008]20 . . . Dielectric Film

[0009]22 . . . Upper Electrode

[0010]24 . . . Smoothing Insulation Film

[0011]26 . . . Insulation Film

[0012]27 . . . Inter-layer Insulation Film

[0013]28 a, 28 d . . . The First Via-hole

[0014]28 b, 28 c, 28 e . . . The Second Via-hole

[0015]30 a, 30 b . . . The First Upper-layer Wiring Layer

[0016]30 b, 30 c, 30 e . . . The Second Upper-layer Wiring Layer

[0017]32 . . . Insulation Dummy Layer

[0018]34 . . . Polysilicon Dummy Layer

TECHNICAL FIELD

[0019] The present invention relates to a semiconductor device and its fabricating method. Particularly, it relates to a semiconductor device in which a capacitance element is mounted on a semiconductor substrate and a method of fabricating the device.

BACKGROUND ART

[0020] A conventional process for fabricating LSI (Large-scale Integrated Circuit) where a capacitance element is formed on a semiconductor substrate will be described with reference to schematic sectional process diagrams of FIG. 39 to FIG. 41.

[0021] To start with, as shown in FIG. 39, a first insulation film 12 and a second insulation film 16 which are made of SiO₂ film or the like are piled in turn on a semiconductor substrate 10.

[0022] Subsequently, using the sputtering method for example, on the second insulation film 16 are piled a Ti layer, a TiON layer, a Ti layer, an Al-Si layer and a TiN layer in turn from below to form a TiN/Al-Si/Ti/TiON/Ti lamination film.

[0023] Subsequently, using CVD (Chemical Vapor Deposition) method for example, on the TiN/Al-Si/Ti/TiON/Ti lamination film is piled a dielectric film of SiO₂, SiN, Ta₂O₅ and the like. Further, using the sputtering method for example, on the dielectric film is piled a conductor layer of a Ti layer, a TiN layer or the like.

[0024] Then, through the photolithographing process and RIT (Reactive Ion Etching) process, these piled conductor layer and dielectric film are selectively removed by etching into a predetermined pattern to form an upper electrode 22 of Ti, TiN and the like on the TiN/Al-Si/Ti/TiON/Ti lamination film through a dielectric film 20 of SiO₂ SiN, Ta₂O₅ or the like.

[0025] Subsequently, through the photolithographing process and RIE process, the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is selectively removed by etching into a predetermined pattern to form a lower electrode 18 d of the TiN/Al-Si/Ti/TiON/Ti lamination film.

[0026] In this way, a capacitance element comprised of the upper electrode 22 and the lower electrode 18 d which sandwich the dielectric film 20 between them is formed.

[0027] Subsequently, using the plasma CVD method for example, which uses TEOS (tetraethoxy silane; Si(OC₂H₅)₄) as raw materials, a SiO₂ film is piled on the whole surface of a base body including the upper electrode 22 and lower electrode 18 d. After the SiO₂ film is further coated with SOG (Spin On Glass) film, a smoothing process that etches back these SOG film and SiO₂ film is performed. In other words, unevenness of the surface of the base body is smoothed by filling with a smoothing insulation film 24 formed of the SiO₂ film and SOG film.

[0028] Note that, on this occasion, because the surface of the upper electrode 22 formed on the lower electrode 18 d lies on a higher level than the surface of the lower electrode 22, the surface of the upper electrode may have sometimes been in a exposed state.

[0029] Next, as shown in FIG. 40, using the plasma CVD method for example, an insulation film 26 made of, e.g. SiO₂ film is piled on the whole surface of the base body including the upper electrode 22 and the smoothing insulation film 24. An inter-layer insulation film 27 is thus formed by the smoothing insulation film 24 and insulation film 26.

[0030] Subsequently, using the photolithographing process and the dry etching method, the inter-layer insulation film 27 on the upper electrode 22 is selectively removed by etching and the inter-layer insulation film 27 on the lower electrode 18 d is also selectively removed by etching to open a first via-hole 28 d and a second via-hole 28 e. At this time, in order to reduce a contact resistance, TiN in the surface of the lower electrode 18 d may sometimes be removed.

[0031] Next, as shown in FIG. 41, after an Al-alloy layer is piled on the whole surface of the base body using the sputtering method for example, the Al-alloy layer is processed using the photolithographing process and the dry etching method to form a first Al-alloy upper layer wiring layer 30 d and a second Al-alloy upper layer wiring layer 30 e that are connected to the upper electrode 22 and the lower electrode 18 d through the first and second via-holes 28 d and 28 e, respectively.

[0032] However, in the conventional process of forming a capacitance element, when the smoothing process to smooth unevenness of the surface of the base body by filling with the smoothing insulation film 24 formed of the SiO₂ film and SOG film is performed after a capacitance element comprised of the upper electrode 22 and lower electrode 18 d that sandwich the dielectric film 20 between them is formed, because the surface of the upper electrode 22 formed on the lower electrode 18 d lies on a higher level than the surface of lower electrode 18 d, the upper electrode 22 and further, even the dielectric film 20 lying thereunder is subjected to etching by the etch-back in the smoothing process. That is to say, in the smoothing process, the upper electrode 22 and further the dielectric film 20 lying thereunder sustain damage.

[0033] Therefore, there is a problem in which characteristics of a capacitance element such as a capacitance value fluctuate or its reliability deteriorates, so that it is impossible to obtain such a capacitance element that has satisfactory characteristics and high reliability.

[0034] Moreover, when the first and second via-holes 28 d and 28 e are opened so as to form the first and second Al-alloy upper layer wiring layers 30 d and 30 e connected respectively to the upper electrode 22 and lower electrode 18 d of a capacitance element, the film thickness of inter-layer insulation film 27 on the upper electrode 22 to be etched for opening the first via-hole 28 d is thicker than the film thickness of inter-layer insulation film 27 on the lower electrode 18 d to be etched for opening the second via-hole 28 e. Thus, when the first and second via-holes 28 d and 28 e are both intended to be opened satisfactorily, excess over-etching on the surface of upper electrode 22 will inevitably take place. As a result, the upper electrode 22 or the dielectric film 20 lying thereunder will sustain damage due to the over-etching.

[0035] Consequently, this point also raises the problem in which the characteristics of capacitance element such as a capacitance value fluctuate or its reliability deteriorates, thus making it impossible to obtain such a capacitance element that has satisfactory characteristics and high reliability.

[0036] Furthermore, the following problem is also raised.

[0037] That is, in a conventional capacitance element, when comparison is made between distances from an area where the upper electrode 22 and lower electrode 18 d are opposed to each other, which effectively functions as a capacitance element, to the first Al-alloy upper layer wiring layer 30 d and to the second Al-alloy upper layer wiring layer 30 e, the distance on the lower electrode side generally tends to be longer than that on the upper electrode side. As a result, the difference between their impedances occurs, thereby posing another problem of further adding to asymmetry in its characteristics.

[0038] When comparison is made between the first and second via-holes 28 d and 28 e in the conventional capacitance element, the depth of the second via-hole 28 e on the lower electrode side is deeper than the depth of the first via-hole 28 d on the upper side electrode side. This further increases the conventional asymmetry of its characteristics.

DISCLOSURE OF INVENTION

[0039] The present invention was made in view of the foregoing points at issue. An object of the present invention is to provide a semiconductor device and its fabricating method capable of preventing the fluctuation in characteristics such as capacitance value or deterioration of reliability by damage caused to the upper electrode or dielectric film during the process of fabricating a capacitance element, and further suppressing an increase of asymmetry in characteristics, thereby allowing a capacitance element with satisfactory characteristics and high reliability to be implemented.

[0040] A semiconductor device according to the present invention comprises: a lower electrode that is formed on a semiconductor substrate through a first insulation film and has a recess form section in which the surface of its periphery lies on a higher level than that of its center; an upper electrode that is formed on the center of the lower electrode through a dielectric film the surface of which lies on a lower level than that of the periphery of lower electrode; and a second insulation film which fills a recess of the lower electrode having a recess form section.

[0041] It should be noted that “the surface lies on a higher level” or “the surface lies on a lower level” used herein is wording to express a level of surface's height with respect to a flat plane of the top or bottom surface of a semiconductor substrate. This definition is hereinafter applied as well.

[0042] The present invention further comprises, in the above semiconductor device, an inter-layer insulation film that is formed as a third insulation film in the periphery of lower electrode, the upper electrode and the second insulation film, a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film, and a second wiring layer that is connected to the periphery of the lower electrode through a second via-hole opened in the inter-layer insulation film.

[0043] A semiconductor device according to the present invention comprises: a lower electrode formed on a semiconductor substrate through a first insulation film; a dummy electrode formed around the lower electrode and having the surface higher than that of the lower electrode; an upper electrode that is formed on the lower electrode through a dielectric film the surface of which lies on a lower level than the top surface of the dummy electrode; and a second insulation layer that fills a recess surrounded by the dummy electrode.

[0044] It should be noted that “a dummy electrode having the surface higher than that of the dielectric film” as described above means that the top surface of the dummy electrode is higher than the surface of the lower electrode with a flat plane of the top or bottom surface of a semiconductor substrate as a reference. A description “the top surface of the dummy electrode” means the uppermost surface of surfaces of the dummy electrode. This definition is hereinafter applied as well.

[0045] The present invention further comprises, in the above semiconductor device, an inter-layer insulation film that is formed as a third insulation film on the dummy electrode, the upper electrode and the second insulation film, a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film, and a second wiring layer that is connected to the periphery of the lower electrode through a second via-hole opened in the inter-layer insulation film.

[0046] A semiconductor device according to the present invention comprises: a lower electrode that is formed on a semiconductor substrate through a first insulation film and has a recess form section in which the surface of its periphery lies on a higher level than that of its center; an upper electrode that is formed on the center of the lower electrode through a dielectric film the surface of which lies on a lower level than that of the periphery of lower electrode; and a second insulation film which fills a recess of the lower electrode having a recess form section and at the same time, covers the surface of the upper electrode.

[0047] The present invention further comprises, in the above semiconductor device, an inter-layer insulation film that is formed as a third insulation film in the periphery of lower electrode, the upper electrode and the second insulation film, a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film, and a second wiring layer that is connected to the periphery of the lower electrode through a second via-hole opened in the inter-layer insulation film.

[0048] A semiconductor device according to the present invention comprises: a lower electrode formed on a semiconductor substrate through a first insulation film; a dummy electrode formed around the lower electrode and having the surface higher than that of the lower electrode; an upper electrode formed on the lower electrode through the dielectric film and the surface of which lies on a lower level than the top surface of the dummy electrode; and a second insulation layer that fills a recess surrounded by the dummy electrode and at the same time, covers the surfaces of the lower and upper electrodes.

[0049] It should be noted that “a dummy electrode having the surface higher than that of the lower electrode” as described above means that the top surface of the dummy electrode is higher than the surface of the lower electrode with a flat plane of the top or bottom surface of a semiconductor substrate as a reference. A description “the top surface of the dummy electrode” means the uppermost surface of surfaces of the dummy electrode. This definition is hereinafter applied as well.

[0050] The present invention further comprises, in the above semiconductor device, an inter-layer insulation film that is formed as a third insulation film on the dummy electrode, the upper electrode and the second insulation film, a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film, and a second wiring layer that is connected to the periphery of the lower electrode through a second via-hole opened in the inter-layer insulation film.

[0051] In the aforementioned semiconductor device, a dummy layer for making a level difference is provided below the periphery of the lower electrode, whereby the lower electrode is formed so as to have a recess form section.

[0052] Also, in the above semiconductor device, a dummy layer for making a level difference is provided below the dummy electrode, whereby the dummy electrode is formed so as to lie on a level higher than the lower electrode.

[0053] Such a dummy layer for making a level difference can be formed of the same material as that of an electrode or a resistance layer of other element in a semiconductor device. The dummy layer for making a level difference can also be formed of an insulation layer.

[0054] According to a semiconductor device of the present invention, because it comprises a lower electrode having a recess form section in which the surface of its periphery lies on a higher level than the surface of its center, and an upper electrode formed on the center of the lower electrode through a dielectric film the surface of which lies on a lower level than that of the periphery of lower electrode, namely, because the surface of dielectric film on the center of lower electrode with a recess form section is lower than that of the periphery of lower electrode, when the second insulation film serving as a smoothing insulation film on the whole surface of base body is formed, even if the smoothing process of etching back an insulation film or the like piled on the whole surface of base body is executed, the periphery of lower electrode forms an etching stopper which can prevent the dielectric film from sustaining damage. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0055] Moreover, in a semiconductor device according to the present invention, the third insulation film is formed on the periphery of lower electrode, the upper electrode and the second insulation film to make an inter-layer insulation film; the first wiring layer connected to the upper electrode through the first via-hole opened in the inter-layer insulation film on the upper electrode being formed; and the second wiring layer connected to the periphery of lower electrode through the second via-hole opened in the inter-layer insulation film on the periphery of lower electrode being formed. Thus, the film thickness of inter-layer insulation film on the upper electrode to be etched for opening the first via-hole is approximately equal to that of inter-layer insulation film on the periphery of lower electrode to be etched for opening the second via-hole. Therefore, when the first and second via-holes are opened, it is possible to prevent the dielectric film under the upper electrode from suffering damage due to an excess overetching to the surface of upper electrode. Consequently, it is possible to obtain a capacitance element which, in addition to the above advantage, has still less fluctuation in its characteristics and higher reliability. Furthermore, in comparing the first via-hole with second via-hole, the depth of the second via-hole opened on the periphery of lower electrode is approximately equal to the depth of the first via-hole opened on the upper electrode. Thus, of the distances from an area where the upper and lower electrodes are opposed to each other and which effectively functions as a capacitance element to the first and second wiring layers, the distance on the lower electrode side which generally tends to be longer than that on the upper electrode side can be shortened. Therefore, it is possible to reduce the difference of their impedances to suppress an increase of asymmetrical characteristics of a capacitance element and thus improve symmetry of characteristics thereof.

[0056] A semiconductor device according to the present invention comprises a lower electrode, a dummy electrode formed around the lower electrode and having the surface higher than that of the lower electrode, and an upper electrode formed on the lower electrode through a dielectric film, wherein the surface of the dielectric film on the lower electrode is lower than the top surface of the dummy electrode around the lower electrode. Thus, when the second insulation film serving as a smoothing insulation film is formed on the whole surface of base body, even if a smoothing process to etch back the insulation film piled on the whole surface of base body is performed the dummy electrode becomes an etching stopper and the dielectric film can be prevented from sustaining damage. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0057] A semiconductor device according to the present invention comprises a lower electrode having a recess form section in which the surface of its periphery is on a higher level than that of its center, and an upper electrode formed on the center of the lower electrode through a dielectric film and having the surface lower than that of the periphery of lower electrode. In other words, the surface of upper electrode on the center of lower electrode having a recess form section is lower than that of the periphery of lower electrode. Thus, when the second insulation film serving as a smoothing insulation film is formed on the whole surface of base body, the surface of the upper electrode is always in a state covered by the second insulation film. As a result, even if a smoothing process to etch back the insulation film piled on the whole surface of base body is executed, together with the fact that the periphery of lower electrode acts as a etching stopper, it is possible to prevent the upper electrode and further the dielectric film thereunder from suffering damage. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0058] Moreover, a semiconductor device according to the present invention further comprises an inter-layer insulation film formed as a third insulation film on a second insulation film covering the periphery of lower electrode and the surface of upper electrode, a first wiring layer connected to the upper electrode through a first via-hole opened in the inter-layer insulation film on the upper electrode, and a second wiring layer connected to the periphery of lower electrode through a second via-hole opened in the inter-layer insulation film on the periphery of lower electrode. Thus, the film thickness of inter-layer insulation film on the upper electrode to be etched for opening a first via-hole is thicker than that of inter-layer insulation film on the periphery of lower electrode to be etched for opening a second via-hole. Consequently, when the first and second via-holes are opened, it is possible to prevent the upper electrode and further a dielectric film thereunder from sustaining damage due to excess overetching to the surface of upper electrode. Therefore, it is possible to obtain a capacitance element which, in addition to the above advantage, has still less fluctuation in its characteristics and high reliability.

[0059] Furthermore, in comparing the first via-hole with second via-hole, the depth of the second via-hole opened on the periphery of lower electrode is shallower than that of the first via-hole opened on the upper electrode. Thus, of distances from an area where the upper electrode and lower electrode are opposed to each other and which functions effectively as a capacitance element to the first and second wiring layers, the distance on the lower electrode side which generally tends to be longer than that on the upper electrode side is shortened. This makes the difference in their impedances small to suppress an increase of asymmetry in characteristics of a capacitance element, thereby allowing symmetry in characteristics of the capacitance element to be improved.

[0060] A semiconductor device according to the present invention comprises a lower electrode, a dummy electrode formed around the lower electrode and having the surface higher than that of the lower electrode, and an upper electrode formed on the lower electrode through a dielectric film, wherein the surface of upper electrode on the lower electrode is lower than the top surface of the dummy electrode around the lower electrode. Thus, when the second insulation film serving as a smoothing insulation film is formed on the whole surface of a base body, the second insulation film makes it possible to cover the surface upper electrode easily. Therefore, even if a smoothing process to etch back the insulation film piled on the whole surface of the base body is executed, it is possible to prevent the upper electrode and further the dielectric film thereunder from sustaining damage as a result of the surface of upper electrode being etched, together with the fact that the dummy electrode acts as a etching stopper. Consequently, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0061] In a case where, in the above semiconductor device according to the present invention, the dummy layer for making a level difference provided below the periphery of lower electrode is formed of the same material as those of electrodes or resistance layers of other elements in the semiconductor device, simplification of its fabrication can be realized. Also, in the case where the dummy layer for making a level difference provided below the dummy electrodes is formed of the same conductor layer as are wiring layers of other elements in the semiconductor device, its fabrication can be simplified.

[0062] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference in the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; piling a conductor film on these first insulation film and dummy layer and then patterning the conductor film so as to form a lower electrode with a recess form section in which the surface of its periphery lies on a higher level than the surface of its center, in the predefined area of forming a capacitance element; forming an upper electrode through a dielectric film the surface of which lies on a lower level than that of the periphery of lower electrode; and forming a second insulation film on the whole surface of a base body to fill a recess of the lower electrode having a recess form section.

[0063] A method of fabricating a semiconductor device according to the present invention further comprises the steps of: forming a third insulation film on the whole surface of a base body including the periphery of the lower electrode, the upper electrode and the second insulation film to form an inter-layer insulation film; opening a first via-hole in the inter-layer insulation film on the upper electrode and also forming a second via-hole in the inter-layer insulation film on the periphery of the lower electrode; and forming a first wiring layer connected to the upper electrode through the first via-hole and also forming a second wiring layer connected to the periphery of the lower electrode through the second via-hole.

[0064] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference in the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; piling a conductor film on these first insulation film and dummy layer and then patterning the conductor film so as to form a lower electrode in the predefined area of forming a capacitance element and forming a dummy electrode in the periphery of the predefined area of forming the capacitance element as covers the dummy layer and has a surface higher than the surface of the lower electrode; and forming an upper electrode on the lower electrode through the dielectric film the surface of which lies on a lower level than the top surface of the dummy electrode; and forming a second insulation film on the whole surface of a base body to

[0065] a recess the periphery of which is surrounded by the dummy electrode.

[0066] A method of fabricating a semiconductor device according to the present invention further comprises the steps of: forming a third insulation film on the whole surface of the base body including the dummy electrode, the upper electrode and the second insulation film to form an inter-layer insulation film; opening a first via-hole in the inter-layer insulation film on the upper electrode and also forming a second via-hole in the inter-layer insulation film in the lower electrode; and forming a first wiring layer connected to the upper electrode through the first via-hole and also forming a second wiring layer connected to the lower electrode through the second via-hole.

[0067] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference around a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; piling a conductor film on these first insulation film and dummy layer and then patterning the conductor film so as to form a lower electrode with a recess section form the surface of which lies on a higher level than the surface thereof in the predefined area of forming the capacitance element; forming an upper electrode, whose surface lies on a lower level than the surface of the periphery of the lower electrode, on the central part of the lower electrode through a dielectric film; and forming a second insulation film on the whole surface of a base body to fill a recess section form of the lower electrode to cover the surface of the upper electrode.

[0068] A method of fabricating a semiconductor device according to the present invention further comprises the steps of: forming a third insulation film on the whole surface of the base body including the dummy electrode and the second insulation film to form an inter-layer insulation film; opening a first via-hole in the inter-layer insulation film on the upper electrode and also opening a second via-hole in the inter-layer insulation film on the lower electrode; and forming a first wiring layer connected to the upper electrode through the first via-hole and also forming a second wiring layer connected to the lower electrode through the second via-hole.

[0069] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference in the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; piling a conductor film on these first insulation film and dummy layer and then patterning the conductor film so as to form a lower electrode in the predefined area of forming a capacitance element and forming a dummy electrode in the periphery of the predefined area of forming the capacitance element as covers the dummy layer and has a surface higher than the surface of the lower electrode; and forming an upper electrode the surface of which lies on a lower level than the top surface of the dummy electrode, on the lower electrode through the dielectric film; and forming a second insulation film on the whole surface of a base body to fill a recess the periphery of which is surrounded by the dummy electrode and also cover the surfaces of the lower and upper electrodes.

[0070] A method of fabricating a semiconductor device according to the present invention further comprises the steps of: forming a third insulation film on the whole surface of the base body including the dummy electrode, the upper electrode and the second insulation film to form an inter-layer insulation film; opening a first via-hole in the inter-layer insulation film on the upper electrode and also forming a second via-hole in the inter-layer insulation film in the lower electrode; and forming a first wiring layer connected to the upper electrode through the first via-hole and also forming a second wiring layer connected to the lower electrode through the second via-hole.

[0071] In the above described method of fabricating a semiconductor device, the process of forming the dummy layer for making a level difference can be combined with the process of forming electrodes or resistance layers of other elements in the semiconductor device. The dummy layer for making a level difference can be formed of an insulation layer.

[0072] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference in the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; patterning a conductor film piled on the dummy layer to form a lower electrode with a recess form section in which the surface of its periphery lies on a higher level than the surface of its center in a predefined area of forming a capacitance element; and forming an upper electrode on the center of lower electrode through a dielectric film the surface of which lies on a lower level than the surface of periphery of lower electrode. Thus, when the second insulation film serving as a smoothing insulation film is formed, even if a smoothing process to etch back the insulation film piled on the whole surface of a base body is executed, the periphery of lower electrode acts as an etching stopper, thereby allowing the dielectric film to be prevented from suffering damage. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0073] Moreover, a method of fabricating a semiconductor device according to the present invention further comprises the steps of: forming a third insulation film on the whole surface of the base body including the periphery of the lower electrode, the upper electrode and the second insulation film to form an inter-layer insulation film; and then forming a first wiring layer connected to the upper electrode through the first via-hole opened in the inter-layer insulation film on the upper electrode and also forming a second wiring layer connected to the periphery of lower electrode through the second via-hole opened in the inter-layer insulation film on the periphery of lower electrode. Thus, the film thickness of the inter-layer insulation film on the upper electrode to be etched for opening the first via-hole becomes approximately equal to the film thickness of the inter-layer insulation film on the periphery of lower electrode to be etched for opening the second via-hole. Therefore, when the first and second via-holes are opened, it is possible to prevent the dielectric film under the upper electrode from sustaining damage due to an excess overetching to the surface of the upper electrode. Consequently, it is possible to obtain a capacitance element having in addition to the above advantage, still less fluctuation in its characteristics and higher reliability.

[0074] In comparing the first via-hole with the second via-hole, the depth of the second via-hole opened on the lower electrode becomes approximately equal to the depth of the first via-hole opened on the upper electrode. Thus, of distances from an area where the upper and lower electrodes are opposed to each other and which effectively functions as a capacitance element to the first and second wiring layers, the distance on the lower electrode side which generally tends to be longer than that on the upper electrode side is shortened. This makes the difference in their impedances decrease to thereby suppress an increase of asymmetry in characteristics of a capacitance element and improve symmetry in characteristics of the capacitance element.

[0075] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference in the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; patterning thereafter a conductor film piled on these first insulation film and dummy layer to form a lower electrode in a predefined area of forming a capacitance element and also form a dummy electrode that covers the dummy layer and has the surface higher than that of the lower electrode around the predefined area of forming a capacitance element; and forming an upper electrode on the lower electrode through a dielectric film the surface of which lies on a lower level than the top surface of the dummy electrode. Thus, when a second insulation film serving as a smoothing insulation film is formed, even if a smoothing process to etch back an insulation film piled up all over the base body is executed, the dummy electrode acts as an etching stopper, whereby it is possible to prevent the dielectric film from sustaining damage. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0076] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference in the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; patterning a conductor film piled on these first insulation film and dummy layer to form a lower electrode with a recess form section in which the surface of its periphery lies on a higher level than the surface of its center; and forming an upper electrode the surface of which lies on a lower level than the surface of the periphery of lower electrode on the center of lower electrode through a dielectric film, whereby it is possible to easily materialize covering the surface of upper electrode by a second insulation film formed on the whole surface of a base body. Thus, when the second insulation film serving as a smoothing insulation film is formed, even if a smoothing process to etch back the insulation film piled on the whole surface of the base body, the periphery of lower electrode becomes an etching stopper, thereby making it possible to avoid that the surface of upper electrode is etched to cause damage to the upper electrode and further the dielectric film thereunder. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0077] Moreover, a method of fabricating a semiconductor device according to the present invention further comprises the steps of: forming a third insulation film on the whole surface of a base body including the periphery of the lower electrode and the second insulation film covering the surface of the upper electrode to form an inter-layer insulation film; and thereafter forming a first wiring layer connected to the upper electrode through a first via-hole opened in the inter-layer insulation film on the upper electrode and also forming a second wiring layer connected to the periphery of lower electrode through a second via-hole opened in the inter-layer insulation film on the periphery of lower electrode. As a result, the film thickness of the inter-layer insulation film on the upper electrode to be etched for opening the first via-hole becomes thicker than that of the inter-layer insulation film on the periphery of lower electrode to be etched for opening the second via-hole. Thus, when the first and second via-holes are opened, it is possible to prevent the upper electrode and further the dielectric film thereunder from suffering damage due to an excess overetching to the surface of upper electrode. Therefore, it is possible to obtain a capacitance element having, in addition to the above advantage, still less fluctuation in its characteristics and higher reliability.

[0078] Also, in comparing the first via-hole with the second via-hole, the depth of the second via-hole opened on the lower electrode becomes shallower than that of the first via-hole opened on the upper electrode. Thus, of distances from an area where the upper and lower electrodes are opposed to each other and which functions effectively as a capacitance element to the first and second wiring layers, the distance on the lower electrode side which generally tends to be longer is made shorter. Therefore, it is possible to reduce the difference in their impedances and suppress an increase of asymmetry in characteristics of a capacitance element, thereby allowing symmetry in characteristics of the capacitance element to be improved.

[0079] A method of fabricating a semiconductor device according to the present invention comprises the steps of: forming a dummy layer with a predetermined thickness for making a level difference around a predetermined area of forming a capacitance element on a semiconductor substrate through a first insulation film; patterning thereafter a conductor film piled on these first insulation film and dummy layer to form a lower electrode in the predefined area of forming a capacitance element and also form a dummy electrode that covers the dummy layer and has the surface higher than the surface of lower electrode around the predefined area of forming a capacitance element; and forming an upper electrode the surface of which lies on a lower level than the top surface of the dummy electrode, on the lower electrode through a dielectric film. As a result, it is possible to easily materialize covering the surface of upper electrode by a second insulation film formed on the whole surface of a base body. Thus, when the second insulation film serving as a smoothing insulation film is formed, even if a smoothing process to etch back the insulation film piled on the whole surface of the base body is executed, the dummy electrode becomes an etching stopper and so it is possible to prevent the upper electrode and further the dielectric film thereunder from sustaining damage. Therefore, it is possible to obtain a capacitance element having less fluctuation in its characteristics and high reliability.

[0080] In the above method of fabricating a semiconductor device according to the present invention, by combining the process of forming the dummy layer for making a level difference with a process of forming an electrode or a resistance layer of another element in a semiconductor device, it is possible to aim at simplifying its fabrication process.

BRIEF DESCRIPTION OF DRAWINGS

[0081]FIG. 1 is a schematic sectional diagram showing a capacitance element according to a first embodiment of the present invention.

[0082]FIG. 2 is a schematic sectional process diagram (No.1) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0083]FIG. 3 is a schematic sectional process diagram (No.2) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0084]FIG. 4 is a schematic sectional process diagram (No.3) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0085]FIG. 5 is a schematic sectional process diagram (No.4) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0086]FIG. 6 is a schematic sectional process diagram (No.5) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0087]FIG. 7 is a schematic sectional process diagram (No.6) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0088]FIG. 8 is a schematic sectional process diagram (No.7) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0089]FIG. 9 is a schematic sectional process diagram (No.8) for explaining the method of fabricating the capacitance element shown in FIG. 1.

[0090]FIG. 10 is a schematic sectional diagram showing a capacitance element according to a second embodiment of the present invention.

[0091]FIG. 11 is a schematic sectional process diagram (No.1) for explaining the method of fabricating the capacitance element shown in FIG. 10.

[0092]FIG. 12 is a schematic sectional process diagram (No.2) for explaining the method of fabricating the capacitance element shown in FIG. 10.

[0093]FIG. 13 is a schematic sectional diagram showing a capacitance element according to a third embodiment of the present invention.

[0094]FIG. 14 is a schematic sectional process diagram (No.1) for explaining the method of fabricating the capacitance element shown in FIG. 13.

[0095]FIG. 15 is a schematic sectional process diagram (No.2) for explaining the method of fabricating the capacitance element shown in FIG. 13.

[0096]FIG. 16 is a schematic sectional process diagram (No.3) for explaining the method of fabricating the capacitance element shown in FIG. 13.

[0097]FIG. 17 is a schematic sectional process diagram (No.4) for explaining the method of fabricating the capacitance element shown in FIG. 13.

[0098]FIG. 18 is a schematic sectional process diagram (No.5) for explaining the method of fabricating the capacitance element shown in FIG. 13.

[0099]FIG. 19 is a schematic sectional process diagram (No.6) for explaining the method of fabricating the capacitance element shown in FIG. 13.

[0100]FIG. 20 is a schematic sectional diagram showing a capacitance element according to a fourth embodiment of the present invention.

[0101]FIG. 21 is a schematic sectional process diagram (No.1) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0102]FIG. 22 is a schematic sectional process diagram (No.2) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0103]FIG. 23 is a schematic sectional process diagram (No.3) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0104]FIG. 24 is a schematic sectional process diagram (No.4) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0105]FIG. 25 is a schematic sectional process diagram (No.5) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0106]FIG. 26 is a schematic sectional process diagram (No.6) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0107]FIG. 27 is a schematic sectional process diagram (No.7) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0108]FIG. 28 is a schematic sectional process diagram (No.8) for explaining the method of fabricating the capacitance element shown in FIG. 20.

[0109]FIG. 29 is a schematic sectional diagram showing a capacitance element according to a fifth embodiment of the present invention.

[0110]FIG. 30 is a schematic sectional process diagram (No.1) for explaining the method of fabricating the capacitance element shown in FIG. 29.

[0111]FIG. 31 is a schematic sectional process diagram (No.2) for explaining the method of fabricating the capacitance element shown in FIG. 29.

[0112]FIG. 32 is a schematic sectional diagram showing a capacitance element according to a sixth embodiment of the present invention.

[0113]FIG. 33 is a schematic sectional process diagram (No.1) for explaining the method of fabricating the capacitance element shown in FIG. 32.

[0114]FIG. 34 is a schematic sectional process diagram (No.2) for explaining the method of fabricating the capacitance element shown in FIG. 32.

[0115]FIG. 35 is a schematic sectional process diagram (No.3) for explaining the method of fabricating the capacitance element shown in FIG. 32.

[0116]FIG. 36 is a schematic sectional process diagram (No.4) for explaining the method of fabricating the capacitance element shown in FIG. 32.

[0117]FIG. 37 is a schematic sectional process diagram (No.5) for explaining the method of fabricating the capacitance element shown in FIG. 32.

[0118]FIG. 38 is a schematic sectional process diagram (No.6) for explaining the method of fabricating the capacitance element shown in FIG. 32.

[0119]FIG. 39 is a schematic sectional process diagram (No.1) for explaining a conventional method of fabricating a capacitance element.

[0120]FIG. 40 is a schematic sectional process diagram (No.2) for explaining the conventional method of fabricating a capacitance element.

[0121]FIG. 41 is a schematic sectional process diagram (No.3) for explaining the conventional method of fabricating a capacitance element.

BEST MODE FOR CARRYING OUT THE INVENTION

[0122] Modes for carrying out the invention, or embodiments of the present invention will be described below with reference to the accompanying drawings.

[0123] (A First Embodiment)

[0124]FIG. 1 is a schematic sectional diagram showing a capacitance element according to a first embodiment of the present invention. FIG. 2 to FIG. 9 are schematic sectional process diagrams for explaining the method of fabricating the capacitance element shown in FIG. 1, respectively.

[0125] As shown in FIG. 1, in the capacitance element according to this embodiment, there is formed a polysilicon dummy layer 14 for making a level difference in the periphery of a predefined area of forming the capacitance element on a semiconductor substrate 10 through a first insulation film 12 made of, e.g. a SiO₂ film. The dummy layer 14 is made of a polysilicon layer having a predetermined thickness of, e.g. 100 nm to 500 nm or so. On the first insulation film 12 and the polysilicon dummy layer 14 is formed a second insulation film 16. Note that the second insulation film 16 can be dispensed with.

[0126] Moreover, on the second insulation film 16 is formed a lower electrode 18 a made of a TiN/Al-Si/Ti/TiON/Ti lamination film or Cu, Al-Cu and the like. In the lamination film, for example a Ti layer with about 5 to 70 nm thickness, a TiON layer with about 10 to 200 nm thickness, a Ti layer with about 5 to 70 nm thickness, an Al-Si layer with about 300 to 1500 nm thickness, and an TiN layer with about 5 to 70 nm thickness are piled in turn from below.

[0127] Specifically, the lower electrode 18 a has a recess form section in which the surface of its periphery on the polysilicon dummy layer 14 with about 100 to 500 nm thickness for making a level difference lies on a higher level than the surface of its center by 100 to 500 nm or so.

[0128] Additionally, in the lower electrode 18 a of such a TiN/Al-Si/Ti/TiON/Ti multilayer, the uppermost TiN layer functions as an antireflection coating in the photolithographing step during its fabrication process and as an antioxidation film of the Al-Si layer thereunder. The Al-Si layer functions as the principal part of electrodes that require a conductive characteristic. The lower Ti/TiON/Ti layered film functions as a barrier metal.

[0129] Furthermore, on the center of the lower electrode 18 a is formed an upper electrode 22 made of Ti, TiN or a Ti/TiN layered film having 5 to 100 nm or so thickness, through a dielectric film 20 made of Ta₂O₅, SiO₂ or SiN and the like, having a predetermined thickness of, e.g. 10 to 300 nm or so, in this embodiment Ta₂O₅ dielectric film. When the dielectric film 20 is formed of ta₂O₅, it is preferable to form the upper electrode 22 out of TiN or a layered film in which TiN and Ti are piled in this order, TiN and the layered film being hard to react with oxygen. When the dielectric film 20 is formed of SiO₂, SiN and the like, the upper electrode 22 can be formed of Ti, TiN or a TiN/Ti layered film.

[0130] In this manner, a capacitance element is formed from the upper electrode 22 and the lower electrode 18 a which sandwich the dielectric film 20 between them.

[0131] Then, the surface of the upper electrode 22 formed on the center of the lower electrode 18 a with a recess form section of this capacitance element becomes lower than the surface of the periphery of lower electrode 18 a with a recess form section over the polysilicon dummy layer 14.

[0132] Moreover, a smoothing process to unevenness of a base body including the upper electrode 22 and lower electrode 18 a is performed. Specifically, a smoothing insulation film 24 comprised of SiO₂ film piled on the whole surface of the base body, for example, using the plasma CVD method with the TEOS as a raw material as well as SOG film coated thereon is formed. This smoothing insulation film 24 fills a recess of the lower electrode 18 a with a recess form section and also covers the surface of upper electrode 22.

[0133] Furthermore, on the smoothed whole surface of the base body, namely, on the periphery of lower electrode 18 a and the smoothing insulation film 24 is piled an insulation film 26 made of, e.g. SiO₂ film. The smoothing insulation film 24 and insulation film 26 form an inter-layer insulation film 27.

[0134] Then, a first upper-layer wiring layer 30 a which is made of, e.g. an Al-alloy layer and connected to the upper electrode 22 is formed through a first via-hole 28 a opened in the inter-layer insulation film 27 on the upper electrode 22.

[0135] Also, a second upper-layer wiring layer 30 b which is made of, e.g. an Al-alloy layer and connected to the periphery of lower electrode 18 a is formed through a second via-hole 28 b opened in the inter-layer insulation film 27 on the periphery of lower electrode 18 a.

[0136] Next, a method of fabrication the capacitance element shown in FIG. 1 will be described with reference to schematic sectional process diagrams of FIG. 2 to FIG. 9.

[0137] To begin with, as shown in FIG. 2, after the first insulation film 12 which is made of, e.g. SiO₂ film is formed on the semiconductor substrate 10, for example, a polysilicon layer with a predetermined thickness, e.g. about 100 to 500 nm thickness is further formed on the first insulation film 12. Subsequently, through the photolithographing process and RIE process, the polysilicon layer is selectively removed by etching to pattern it into a predetermined shape.

[0138] In this way, a polysilicon dummy layer 14 made of a polysilicon layer of about 100 to 500 nm thickness for making a level difference is formed on the periphery of a predefined area of forming a capacitance element on the semiconductor substrate 10 through the first insulation film 12.

[0139] It is noted that the process of forming the polysilicon dummy layer 14 can be combined with the process of forming a polysilicon layer used as a gate electrode of other elements, e.g. MOSTr (Metal Oxide Semiconductor Transistor), a resistance layer of a resistance element, and an electrode of BipTr (bipolar transistor) in LSI.

[0140] Next, as shown in FIG. 3, the second insulation film 16 is formed on the whole surface of a base body including the polysilicon dummy layer 14 for making a level difference. Note that the second insulation film 16 may be omitted to form.

[0141] Next, as shown in FIG. 4, using the sputtering method for example, a conductor film with a predetermined thickness is formed. For example, the conductor film is a TiN/Al-Si/Ti/TiON/Ti lamination film 18 comprised of a Ti layer with about 5 to 70 nm thickness, a TiON layer with about 10 to 200 nm thickness, a Ti layer with about 5 to 70 nm thickness, an Al-Si layer with about 300 to 1500 nm thickness, and a TiN layer with about 5 to 70 nm thickness which are piled in turn from below.

[0142] Additionally, in such a multilayered structure, the uppermost TiN layer functions as an antireflection coating in the photolithographing step during the fabrication process and as an antioxidation film of the Al-Si layer lying thereunder. The lower Ti/TiON/Ti lamination film functions as a barrier metal.

[0143] Also, in the TiN/Al-Si/Ti/TiON/Ti lamination film 18, the surface of polysilicon dummy layer 14 with about 100 to 500 nm thickness for making a level difference is higher than the surface of an area surrounded by the polysilicon dummy layer 14 by 100 to 500 nm or so.

[0144] Next, as shown in FIG. 5, a dielectric film made of Ta₂O₅, SiO₂, SiN and the like, in this embodiment Ta₂O₅ dielectric film is piled on the TiN/Al-Si/Ti/TiON/Ti lamination film 18, using the CVD method for example, up to a predetermined thickness of, e.g. 10 to 300 nm or so. Further using the sputtering method for example, a conductor layer made of, e.g. a Ti layer, a TiN layer or a Ti/TiN layered film is piled on the dielectric film up to a predetermined thickness of, e.g. 5 to 100 nm or so.

[0145] Subsequently, through the photographing process and RIE process, these layered conductor layer and dielectric film are selectively removed by etching into a predetermined pattern.

[0146] In this manner, an upper electrode 22 made of a Ti layer, or a Ti/TiN layered film having a thickness of about 5 to 100 nm is formed on the TiN/Al-Si/Ti/TiON/Ti lamination film 18 in the area surrounded by the polysilicon dummy layer 14 through the dielectric film 20 having a thickness of about 10 to 300 nm.

[0147] Note that the surface of the upper electrode 22 at this time is lower in height than the surface of a portion of the lamination film 18 situated over the polysilicon dummy layer 14.

[0148] Next as shown in FIG. 6, through the photolithographing process and RIE process, the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is selectively removed by etching into a predetermined pattern.

[0149] A lower electrode 18 a made of the TiN/Al-Si/Ti/TiON/Ti lamination film is thus formed. It has a recess form section in which the surface of its periphery over the polysilicon dummy layer 14 for making a level difference lies on a higher level than the surface of its center where the upper electrode 22 is formed. In addition, at the same time with forming the lower electrode 18 a, a lower wiring layer (not shown) made of a TiN/Al-Si/Ti/TiON/Ti lamination film of other elements in LSI is formed.

[0150] In this manner, a capacitance element is formed. It is comprised of the upper electrode 22 and lower electrode 18 a that sandwich the dielectric film 20 between them.

[0151] Additionally, the surface of upper electrode 22 of the capacitance element at this time is lower in height than the surface of the periphery of lower electrode 18 a situated over the polysilicon dummy layer 14.

[0152] Next, as shown in FIG. 7, a smoothing process to smooth unevenness of the whole surface of the base body is executed. Specifically, using the plasma CVD method for example, taking the TEOS as a raw material, on the whole surface of the base body including the upper electrode 22 and lower electrode 18 a is piled, for example, a SiO₂ film up to a thickness of 300 to 1500 nm or so. In addition, the SiO₂ film is coated with a SOG film. Thereafter, these SOG film and SiO₂ film are etched back.

[0153] A smoothing insulation film 24 is thus formed. It fills a recess of the lower electrode 18 a having a recess form section and also covers the surface of upper electrode 22 to smooth the whole surface of base body.

[0154] It is noted that, in the process of smoothing the whole surface of base body, namely, the process of forming the smoothing insulation film 24, the surface of upper electrode 22 formed on the center of lower electrode 18 a with a recess form section is lower in level than the surface of the periphery of lower electrode 18 a with a recess form section situated over the polysilicon dummy layer 14. Also, in a general smoothing etch-back, the etching rate of SiO₂ is not so different from those of Ti and TiN, so that in the etch-back after the SOG film and SiO film are formed, although the surface of the periphery of lower electrode 18 a is exposed, the surface of upper electrode 22 is always covered with the smoothing insulation film 24 and thus never be exposed by the etching. In other words, the upper electrode 22 and the dielectric film 20 thereunder will never sustain damage.

[0155] Next, as shown in FIG. 8, using the plasma CVD method for example, on the whole surface of base body including the periphery of lower electrode 18 a and the smoothing insulation film 24 is piled an insulation film 26 made of, e.g. SiO₂ film. The smoothing insulation film 24 and insulation film 27 form an inter-layer insulation film 27.

[0156] Subsequently, using the photolithographing process and dry etching method, the inter-layer insulation film 27 on the upper electrode 22 is selectively removed by etching and also the inter-layer insulation film 27 on the periphery of lower electrode 18 a is selectively removed by etching to open a first via-hole 28 a and a second via-hole 28 b, respectively. On this occasion, in order to decrease the contact resistance, only TiN layer on the surface of lower electrode 18 a may sometimes be removed.

[0157] It is noted at this time that a total film thickness of the inter-layer insulation film 27 on upper electrode 22 to be etched for opening the first via-hole 28 a is thicker than a film thickness of the inter-layer insulation film 26 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. For this reason, when these first and second via-holes 28 a and 28 b are opened, an excess overetching to the surface of upper electrode 22 will never happen.

[0158] Next, as shown in FIG. 9, after an Al-alloy layer is piled using the sputtering method for example, the Al-alloy layer is processed using the photolithographing process and dry etching method to form a first upper-layer wiring layer 30 a and a second upper-layer wiring layer 30 b which are made of the Al-alloy layer and connect respectively to the upper electrode 22 and the periphery of lower electrode 18 a through the first and second via-holes 28 a and 28 b.

[0159] Simultaneously with the formation of the first and second upper-layer wiring layers 30 a and 30 b, upper-layer wiring layers (not shown) of other elements in LSI are formed.

[0160] As described above, in this embodiment, the polysilicon dummy layer 14 for making a level difference, which is made of a polysilicon layer having a thickness of about 100 to 500 nm is formed on the periphery of a predefined area of forming the capacitance element on the semiconductor substrate 10; the second insulation film 16 being formed on the whole surface of base body including the polysilicon dummy layer 14; the lower electrode 18 a having a recess form section in which the surface of its periphery situated over the polysilicon dummy layer 14 lies on a higher level than the surface of its center being formed on the second insulation film 16; the upper electrode 22 having a predetermined thickness of, e.g. about 10 to 300 nm, and the surface of upper electrode 22 being made lower than the surface of the periphery of lower electrode 18 a situated over the polysilicon dummy layer 14. Thus, when the smoothing process in which SiO₂ film is piled on the whole surface of the base body, further coated with SOG film and then they are etched back, the smoothing insulation film 24 which fills the recess of lower electrode 18 a with a recess form section to smooth the whole surface of base body covers the surface of upper electrode 22 at all times. Therefore, the upper electrode 22 and further the dielectric film 20 thereunder will never sustain damage due to the etching in the smoothing process. Consequently, it is possible to suppress the fluctuation in characteristics such as a capacitance value or the like of a capacitance element and the deterioration of reliability thereof, thus allowing a capacitance element having satisfactory characteristics and high reliability to be obtained.

[0161] Moreover, when the first and second via-holes 28 a and 28 b are respectively opened in order to form the first and second upper-layer wiring layers 30 a and 30 b connecting to the respective upper electrode 22 and lower electrode 18 a of a capacitance element, a total film thickness of the inter-layer insulation film 27 on upper electrode 22 to be etched for opening the first via-hole 28 a is thicker than a film thickness of the inter-layer insulation layer 26 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. Thus, an excess overetching to the surface of upper electrode 22 will never take place and so the upper electrode 22 and Ta₂O₂ dielectric film 20 lying thereunder will never suffer damage. Therefore, it is possible to further suppress the fluctuation in characteristics such as a capacitance element or the like and the deterioration of reliability thereof, thus enabling capacitance element having better characteristics and higher reliability to be obtained.

[0162] Furthermore, in comparison between the first and second via-holes 28 a and 28 b, the depth of the second via-hole 28 b opened on the lower electrode 18 a is shallower than that of the first via-hole 28 a on the upper electrode 22. Thus, of distances from an area where the upper electrode 22 and lower electrode 18 a are opposed and which functions effectively as a capacitance element to the first and second upper-layer wiring layers 30 a and 30 b, the distance on the lower electrode side which generally tends to be longer than that on the upper electrode side is made shorter. Therefore, it is possible to reduce a difference in their impedances to suppress an increase of asymmetry in characteristics of a capacitance element, namely, improve a symmetry in characteristics thereof.

[0163] (A Second Embodiment)

[0164]FIG. 10 is a schematic sectional diagram showing a capacitance element according to a second embodiment of the present invention. FIG. 11 and FIG. 12 are schematic sectional process diagrams for explaining a method of fabricating the capacitance element shown in FIG. 10, respectively. It is noted herein that the same elements as constituent elements of the capacitance element of the first embodiment shown in FIG. 1 to FIG. 9 are denoted by the same reference numerals and the description thereof is omitted.

[0165] As shown in FIG. 10, the capacitance element according to this embodiment is characterized by comprising a dummy layer 32 for making a level difference, which is an insulation dummy layer made of SiN, SiO₂ or the like having a predetermined thickness, for example, made of a SiN layer having a thickness of 100 to 500 nm or so, instead of the polysilicon dummy layer 14 for making a level difference in the capacitance element according to the first embodiment shown in FIG. 1. The other constituent elements are the same as in the case of the first embodiment.

[0166] Next, a method of fabricating the capacitance element shown in FIG. 10 will be described with reference to schematic sectional process diagrams of FIGS. 11 and 12.

[0167] To start with, as shown in FIG. 11, after the first insulation film 12 made of, e.g. a SiO₂ film is formed on the semiconductor substrate 10, on the first insulation film 12 is further formed an insulation film of a different kind from the first insulation film 12, e.g. a SiN film having a thickness of 100 to 500 nm or so. Subsequently, by the photolithographing process and etching process, the SiN film is selectively removed by etching into a predetermined pattern.

[0168] In this manner, a SiN dummy layer 32 made of a SiN film having a thickness of 100 to 500 nm or so is formed on the periphery of a predefined area of forming a capacitance element on the semiconductor substrate 10 through the first insulation film 12.

[0169] Next, as shown in FIG. 12, the second insulation film 16 is formed on the whole surface of the base body including the SiN dummy layer 32 in the same way as processes of the first embodiment shown in FIG. 3 to FIG. 9. On the second insulation film 16 is formed a TiN/Al-Si/Ti/TiON/Ti lamination film 18 on which an upper electrode 22 is formed through the dielectric film 20. By the photolithographing process and RIE process, the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is patterned to form the lower electrode 18 a having a recess form section in which the surface of its periphery situated over the SiN dummy layer 32 lies on a higher level than the surface of its center where the upper electrode 22 is formed.

[0170] In this way, the capacitance element comprised of the upper electrode 22 and lower electrode 18 a that sandwich the dielectric film 20 between them is formed.

[0171] Note that the surface of the upper electrode 22 of the capacitance element at this time is lower in level than the surface of the periphery of lower electrode 18 a situated over the SiN dummy layer 32.

[0172] Subsequently, SiO₂ film is piled on the whole surface of base body including the upper electrode 22 and lower electrode 18 a and further coated with SOG film. Thereafter, the smoothing process to etch back these SOG film and SiO₂ film is executed to fill the recess of lower electrode 18 a having a recess form section and also cover the surface of upper electrode 22 for forming the smoothing insulation film 24 that smooths the whole surface of base body.

[0173] It is noted that, in the smoothing process of the whole surface of base body, i.e. the forming process of the smoothing insulation film 24, the surface of upper electrode 22 formed on the center of lower electrode 18 a with a recess form section is lower in level than the surface of the periphery of lower electrode 18 a with a recess form section situated over the SiN dummy layer 32. Under a general smoothing etch-back condition an etch rate difference between SiO₂ and Ti or TiN is not great. Thus, when the SOG film and SiO₂ film are etched back, although the surface of the periphery of lower electrode 18 a is exposed, the surface of upper electrode 22 is always covered with the smoothing insulation film 24 and will never be exposed by etching.

[0174] Subsequently, on the whole surface of base body including the periphery of lower electrode 18 a and the smoothing insulation film 24 is piled the insulation film 26 made of, e.g. SiO₂ film to form the inter-layer insulation film 27 comprises of the smoothing insulation film 24 and the insulation film 26. Then, the inter-layer insulation on film 27 on upper electrode 22 is selectively removed etching and also the inter-layer insulation film 27 on the periphery of lower electrode 18 a is selectively removed by etching for opening the first and second via-holes 28 a and 28 b. The TiN layer of the surface of lower electrode 18 a may sometimes be removed.

[0175] It is noted that a total film thickness at this time of the inter-layer insulation film 27 on upper electrode 22 to be etched for opening the first via-hole 28 a is thicker than a film thickness of the inter-layer insulation film 26 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. For this reason, when these first and second via-holes 28 a and 28 b are opened, the surface of upper electrode 22 will never be subjected to an excess overetching.

[0176] Subsequently, the first and second upper-layer wiring layers 30 a and 30 b are formed, which are respectively connected to the upper electrode 22 and the periphery of lower electrode through the first and second via-holes 28 a and 28 b.

[0177] As described above, in this embodiment, the SiN dummy layer 32 having a predetermined thickness of e.g. 100 to 500 nm or so for making a level difference is formed on the periphery of a predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12; the second insulation film 16 being formed on the whole surface of base body including the SiN dummy layer 32; the lower electrode 18 a having a recess form section in which the surface of its periphery situated over the SiN dummy layer 32 lies on a higher level than the surface of its center being formed on the second insulation film 16; and the upper electrode 22 being formed on the center through the dielectric film 20 so that the surface of upper electrode 22 being formed on the center through the dielectric film 20 so that the surface of upper electrode 22 may be lower in level than the surface of periphery of lower electrode 18 a situated over the SiN dummy layer 32. Thus, when the smoothing process is executed, which etches back after SiO₂ film is piled on the whole surface of base body and further coated with SOG film, the smoothing insulation film 24 which smooths the whole surface of base body by filling the recess of lower electrode 18 a having a recess form section covers the surface of upper electrode 22 at all times. Therefore, the upper electrode 22 and further the dielectric film 20 thereunder will never sustain damage due to the etching in smoothing process. In consequence, similarly to the case of the first embodiment, it is possible to suppress the fluctuation in characteristics such as a capacitance value or the like and the deterioration of reliability on a capacitance element, thus allowing a capacitance element with satisfactory characteristics and high reliability to be obtained.

[0178] Moreover, when the first and second via-holes 28 a and 28 b are opened so as to form the first and second upper-layer wiring layers 30 a and 30 b connected respectively to the upper electrode 22 and lower electrode 18 a of the capacitance element, a total film thickness of the inter-layer insulation film 27 on the upper electrode 22 to be etched for opening the first via-hole 28 a is thicker than a film thickness of the inter-layer insulation film on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. This means that an excess overetching to the surface of upper electrode 22 will never happen and so the upper electrode 22 and further the dielectric film 20 thereunder will never suffer damage. Therefore, just like the case of the first embodiment, it is possible to further suppress the fluctuation in characteristics such as a capacitance value or the like and the deterioration of reliability on a capacitance element, thus allowing a capacitance element with better characteristics and a higher reliability to be obtained.

[0179] Furthermore, the depth of the second via-hole 28 b opened on the lower electrode 18 a is shallower than the depth of the first via-hole 28 a opened on the upper electrode 22. Due to this fact, of distances from an area where the upper electrode 22 and lower electrode 18 a are opposed and which effectively functions as a capacitance element to the first and second upper-layer wiring layers 30 a and 30 b, a distance on the lower electrode side which generally tends to be longer than that on the upper electrode side is made shorter. For this reason, similarly to the case of the first embodiment, it is possible to suppress an increase of asymmetry in characteristics of a capacitance element by reducing the difference in their impedances and so improve symmetry in characteristics of the capacitance element.

[0180] Additionally, in the second embodiment, a SiN dummy layer 32 having a predetermined thickness of, e.g. 100 to 500 nm or so for making a level difference is formed on the periphery of a predefined area of forming a capacitance element on the semiconductor substrate 10 through the first insulation film 12. However, instead of forming such a SiN dummy layer 32, the first insulation film 12 in the center of the predefined area of forming a capacitance element on the semiconductor substrate 10 may selectively be removed by etching through the photolithographing process and etching process to form a recess having a depth of 100 to 500 nm or so. In addition, the selective etching of the first insulation film 12 may be combined with forming the dummy layer 32(or the dummy layer 14, a dummy layer 34 described below) so as to form a final dummy layer and thus form the recess having a depth of 100 to 500 nm or so.

[0181] In any of these cases, similarly to the case of the above second embodiment, it is possible to form the second insulation film 16 on the first insulation film 12 in which the recess with a depth of 100 to 500 nm or so is formed in the center of the predefined area of forming the capacitance element; form a TiN/Al-Si/Ti/TiON/Ti lamination film 18 on the second insulation from 16; pattern this TiN/Al-Si/Ti/TiON/Ti lamination film 18; and thereby form the lower electrode 18 a having a recess form section in which the surface of its periphery lies on a higher level than the surface of its center situated above the recess formed on the first insulation film 12. Therefore, the same function and result as the case of the second embodiment can be effected.

[0182] (A Third Embodiment)

[0183]FIG. 13 is a schematic sectional diagram showing a capacitance element according to a third embodiment of the present invention. FIG. 14 to FIG. 19 are schematic sectional process diagrams for explaining a method of fabricating the capacitance element shown in FIG. 13, respectively. It is noted herein that the same elements as constituent element of the capacitance element shown in FIG. 1 to FIG. 9 of the first embodiment are denoted by the same reference numerals to omit the description thereof.

[0184] As shown in FIG. 13, in comparison with the capacitance element of the first embodiment shown in FIG. 1, a capacitance element according to this embodiment is characterized in that, in stead of the polysilicon dummy layer 14 for making a level difference being formed on the periphery of a capacitance element, a polysilicon dummy layer 34 having the same thickness of, e.g. 100 to 500 nm or so for making a level difference is formed in the circumference of a capacitance element.

[0185] Moreover, it is also characterized in that, in stead of the lower electrode 18 a with a recess form section made of, e.g. TiN/Al-Si/Ti/TiON/Ti multilayer of the first embodiment shown in FIG. 1, a lower electrode 18 b having a flat surface and made of, e.g. TiN/Al-Si/Ti/TiON/Ti multilayer is formed. Separately from the lower electrode 18 b, a dummy electrode 18 c made of, e.g. TiN/Al-Si/Ti/TiON/Ti multilayer and having a higher surface than that of upper electrode 22 is formed over the polysilicon dummy layer 34 for making a level difference surrounding the capacitance element.

[0186] Thus, in contrast with the first embodiment in which the smoothing insulation film 24 filling the recess of lower electrode 18 a with a recess form section covers the surface of upper electrode 22, the smoothing insulation film 24 in this embodiment filling the recess surrounded by the dummy electrode 18 c covers the surface of upper electrode 22 formed above the lower electrode 18 b.

[0187] The other constituent elements are nearly the same as in the first embodiment.

[0188] Next, a method of fabricating the capacitance element shown in FIG. 13 will be described with reference to schematic sectional process diagrams of FIG. 14 to FIG. 19.

[0189] To start with, as shown in FIG. 14, after the first insulation film 12 made of, e.g. a SiO₂ film is formed on the semiconductor substrate 10, on the first insulation film 12 is further formed, e.g. a polysilicon layer having a predetermined thickness of, e.g. 100 to 500 nm or so. Subsequently, by the photolithographing process and RIE process, the polysilicon layer is selectively removed by etching into a predetermined pattern.

[0190] In this manner, the polysilicon dummy layer 34 made of a polysilicon layer with a thickness of 100 to 500 nm or so is formed on the periphery of the predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12.

[0191] Note that the forming process of the polysilicon dummy layer 34 can be combined with the forming process of polysilicon layers used as a gate electrode of other element, e.g. MOSTr, a resistance layer of a resistance element, and an electrode of BipTr in LSI.

[0192] Next, as shown in FIG. 15, in the same way as processes of the first embodiment shown in FIG. 3 to FIG. 5, the second insulation film 16 is formed on the whole surface of the base body including the polysilicon dummy layer 34 for making a level difference. The insulation film 16 may be omitted to form. Then, on the second insulation film 16 is formed TiN/Al-Si/Ti/TiON/Ti lamination film or a layered film made of Cu, Al-Cu and the like, in this embodiment a TiN/Al-Si/Ti/TiON/Ti lamination film 18. On the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is formed the upper electrode 22 made of a Ti layer, a TiN layer or a Ti/TiN layered film through the dielectric film 20 made of Ta₂O₅, SiO₂, SiN and the like, in this embodiment Ta₂O₅.

[0193] Additionally, the surface of upper electrode 22 at this time is lower in level than the top surface of the TiN/Al-Si/Ti/TiON/Ti lamination film 18 situated over the polysilicon dummy layer 34.

[0194] Next, as shown in FIG. 16, through the photolithographing process and RIE process, the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is selectively removed by etching into a predetermined pattern.

[0195] In this way, the lower electrode 18 b made of a TiN/Al-Si/Ti/TiON/Ti lamination film is formed in the predefined area of forming the capacitance element on the second insulation film 16 and also, separately from the lower electrode 18 b, the dummy electrode 18 c made of the TiN/Al-Si/Ti/TiON/Ti lamination film is formed over the polysilicon dummy layer 34 surrounding the predefined area of forming the capacitance element. The dummy layer 18 c has the top surface higher than the surface of lower electrode 18 b.

[0196] Simultaneously with forming the lower electrode 18 b, a lower-layer wiring layer (not shown) made of the TiN/Al-Si/Ti/TiON/Ti lamination film of other element in LSI is formed.

[0197] The capacitance element comprised of the upper electrode 22 and lower electrode 18 b that sandwich the dielectric film 20 between them is thus formed.

[0198] Note that the surface of upper electrode 22 of capacitance element at this time is lower in level than the top surface of dummy electrode 18 c surrounding the area forming the capacitance element and lying over the polysilicon dummy layer 34.

[0199] Next, as shown in FIG. 17, a SiO₂ film having a thickness of 300 to 1500 nm or so is piled on the whole surface of base body including the upper electrode 22 and lower electrode 18 b and is further coated with a SOG film. Thereafter, the smoothing process to etch back these SOG film and SiO₂ film takes place.

[0200] In this manner, the smoothing insulation film 24 is formed, which smooths the whole surface of base body by filling the recess surrounded by dummy electrode 18 c and also covering the surface of upper electrode 22 and lower electrode 18 b.

[0201] Additionally, in the process of smoothing the whole surface of base body, i.e. the process of forming the smoothing insulation film 24, the surface of upper electrode 22 formed on the lower electrode 18 b is lower in level than the top surface of dummy electrode 18 c surrounding the area of forming the capacitance element and lying over the polysilicon dummy layer 34. For this reason, when the SOG film and SiO₂ film are etched back, the surface of lower electrode 18 b and also the surface of upper electrode 22 are always covered with the smoothing insulation film 24 and will never be exposed by etching.

[0202] Next, as shown in FIG. 18, using the plasma CVD method for example, on the whole surface of base body including the dummy electrode 18 c and smoothing insulation film 24 is piled the inter-layer insulation film 27.

[0203] Subsequently, using the photolithographing process and dry etching method, the inter-layer insulation film 27 on the upper electrode 22 and lower electrode 18 b is selectively removed by etching to open the first and second via-holes 28 a and 28 c.

[0204] Next, as shown in FIG. 19, after, e.g. Al-alloy layer is piled by the sputtering method for example, the Al-alloy layer is processed, using the photolithographing process and dry etching method, to form the first and second upper-layer wiring layers 30 a and 30 c made of the Al-alloy layer and each connected to the upper electrode 22 and the periphery of lower electrode 18 b through the first and second via-holes 28 a and 28 c.

[0205] Also, simultaneously with forming the first and second upper-layer wiring layers 30 a and 30 c, upper layer wiring layers (not shown) of other elements in LSI are formed.

[0206] As described above, in this embodiment, the polysilicon dummy layer 34 having a thickness of 100 to 500 nm or so for making a level difference is formed on the periphery of the predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12; the lamination film 18 made of, e.g. a TiN/Al-Si/Ti/TiON/Ti multilayer being formed on the whole surface of base body including the polysilicon dummy layer 34 through the second insulation film 16 to be patterned into a predetermined shape, thereby forming the lower electrode 18 b made of the TiN/Al-Si/Ti/TiON/Ti multilayer in the predefined area of forming the capacitance element; and the dummy electrode 18 c made of the TiN/Al-Si/Ti/TiON/Ti multilayer having the surface higher than the surface of lower electrode 18 b being formed over the polysilicon dummy layer 34 surrounding the lower electrode 18 b. At the same time, the upper electrode 22 is formed on the lower electrode 18 b through the dielectric film 20 so that the surface of upper electrode 22 may be lower in level than the top surface of dummy electrode 18 c situated over the polysilicon dummy layer 34. Thus, when SiO₂ film that is piled on the whole surface of base body and further coated with SOG film is etched back to perform the smoothing process the smoothing insulation film 24 which fills the recess surrounded by the dummy electrode 18 c to smooth the whole surface of base body covers the surface of upper electrode 22 at all times. For this reason, the upper electrode 22 and further the dielectric film 20 lying thereunder will never sustain damage due to etching in the smoothing process. Therefore, similarly to the case of the first embodiment, it is possible to suppress the fluctuation in characteristics such as a capacitance value or the like and the deterioration of reliability of a capacitance element, thus enabling a capacitance element having satisfactory characteristics and high reliability to be obtained.

[0207] Additionally, in the first to third embodiments described above, the case where the lower electrode 18 a or 18 b is connected to the second upper-layer wiring layer 30 b or 30 c through the second via-hole 28 b or 28 c is described. However, there are cases where the lower electrode 18 a or 18 b also serve as a wiring layer and connect to other element in LSI.

[0208] In this case, it is unnecessary that the inter-layer insulation film 27 on the lower electrode 18 a or 18 b is selectively removed by etching to open the second via-hole 28 b or 28 c.

[0209] Moreover, the first and second upper-layer wiring layers 30 a, 30 b or 30 c may be formed in the following way. After a W (tungsten)-layer is piled using the CVD method instead of piling and processing the Al-alloy layer, the W layer is etched back to form a W-plug which fills the first and second via-holes 28 a, 28 b or 28 c. Further, an Al-alloy layer is piled by the sputtering method and then the Al-alloy layer is processed using the photolithographing process and dry etching method to form the first and second upper-layer wiring layers which connect to the W-plug inside the first and second via-holes 28 a, 28 b or 28 c.

[0210] (A Fourth Embodiment)

[0211]FIG. 20 is a schematic sectional diagram showing a capacitance element according to a fourth embodiment of the present invention. FIG. 21 to FIG. 28 are schematic sectional process diagrams for explaining a method of fabricating the capacitance element shown in FIG. 20.

[0212] As shown in FIG. 20, in the capacitance element according to this embodiment, the polysilicon dummy layer 14 made of a polysilicon layer having a predetermined thickness of, e.g. 100 to 500 nm or so for making a level difference is formed on the periphery of the predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12 made of, e.g. a SiO₂ film. On the first insulation film 12 and the polysilicon dummy layer 14 is formed the second insulation film 16. Additionally, the second insulation film 16 can be dispensed with.

[0213] Further, on the second insulation film 16 is formed the lower electrode 18 a made of the TiN/Al-Si/Ti/TiON/Ti lamination film or Cu, Al-Cu and the like. The lamination film is such that a Ti layer having a thickness of, e.g. about 5 to 70 nm, a TiON layer having a thickness of, e.g. about 10 to 200 nm, a Ti layer having a thickness of, e.g. about 300 to 1500 nm, and a TiN layer having a thickness of, e.g. about 5 to 70 nm are piled in turn from below. In this embodiment, the lower electrode 18 a of TiN/Al-Si/Ti/TiON/Ti lamination film is formed.

[0214] In other words, in the lower electrode 18 a having a recess form section, the surface of its periphery situated over the polysilicon dummy layer 14 having a thickness of, e.g. 100 to 500 nm or so for making a level difference lies on a higher level than the surface of its center by 100 to 500 nm or so.

[0215] It is noted that, in the lower electrode 18 a having such a Tin/Al-Si/Ti/TiON/Ti multilayer structure, the uppermost TiN layer functions as an antireflection coating in the photolithographing step during the fabrication process and as an antioxidation film of the Al-Si layer thereunder. The Al-Si layer functions as the principal part of the electrode needing a conductive characteristic. The lower Ti/TiON/Ti lamination film functions as a barrier metal.

[0216] Moreover, on the center of lower electrode 18 a is formed the upper electrode 22 having a thickness of 5 to 100 nm or so, made of a Ti layer, a TiN layer or a Ti/TiN layered film, through the dielectric film 20 having a predetermined thickness of, e.g. 10 to 300 nm or so and made of Ta₂O₅, SiO₂, SiN or the like, in this embodiment Ta₂O₅ dielectric film. When the dielectric film 20 is made of Ta₂O₅, it is preferable to form the upper electrode 22 out of a TiN layer or a layered film in which TiN and Ti are piled in this order those being hard to react with oxygen. When the dielectric film 20 is made of SiO₂, SiN and the like, the upper electrode 22 can be formed out of a Ti layer, a TiN layer or a TiN/Ti layered film.

[0217] In this way, the capacitance element is formed from the upper electrode 22 and lower electrode 18 a which sandwich the dielectric film 20 between them.

[0218] Then, the surface of dielectric film 20 formed on the center of lower electrode 18 a with a recess form section of the capacitance element is lower in level than the surface of the periphery of lower electrode 18 a with a recess form section situated over the polysilicon dummy layer 14.

[0219] Furthermore, the smoothing process to smooth unevenness of the surface of base body including the upper electrode 22 and lower electrode 18 a takes place. Specifically, using the plasma CVD method for example, taking the TEOS as a raw material, the smoothing insulation film 24 made of SiO₂ film piled on the whole surface of base body and SOG film coated thereon is formed. The smoothing insulation film 24 fills the recess of the lower electrode 18 a having a recess form section.

[0220] Also, on the whole surface of the smoothed base body, namely, on the periphery of lower electrode 18 a and the smoothing insulation film 24, the insulation film 26 made of, e.g. SiO₂ film is piled. The smoothing insulation film 24 and the insulation film, 26 form the inter-layer insulation film 27 together.

[0221] In addition, the first upper-layer wiring layer 30 a made of, e.g. an Al-alloy layer and connected to the upper electrode 22 is formed through the first via-hole 28 a opened in the inter-layer insulation film 27 on the upper electrode 22.

[0222] Also, the second upper-layer wiring layer 30 b made of, e.g. an Al-alloy layer and connected to the periphery of lower electrode 18 a is formed through the second via-hole 28 b opened in the inter-layer insulation film 27 on the periphery of lower electrode 18 a.

[0223] Next, a method of fabricating the capacitance element shown in FIG. 20 will be described with reference to schematic sectional process diagrams of FIG. 21 to FIG. 28.

[0224] Initially, as shown in FIG. 21, after the first insulation film 12 made of, e.g. SiO₂ film is formed on the semiconductor substrate 10, further on the first insulation film 12 is formed, e.g. a polysilicon layer having a predetermined thickness of, e.g. 100 to 500 nm. Subsequently, by the photolithographing process and RIE process, the polysilicon layer is selectively removed by etching to pattern into a predetermined shape.

[0225] In this manner, the polysililcon dummy layer 14 made of a polysilicon layer having a thickness of 100 to 500 nm or so is formed on the periphery of the predefined area of forming the capacitance element on the semiconductor substrate 10 though the first insulation film 12.

[0226] It is noted that the forming process of the polysilicon dummy layer 14 can be combined with the forming process of a polysilicon layer used as a gate electrode of other element, e.g. MOSTr(metal oxide semiconductor transistor), a resistance layer of a resistance element, and an electrode of BipTr (bipolar transistor) in LSI.

[0227] Next, as shown in FIG. 22, on the whole surface of base body including the polysilicon dummy layer 14 for making a level difference is formed the second insulation film 16. Note that the second insulation film 16 can be omitted to form.

[0228] Next, as shown in FIG. 23, using the sputtering method for example, on the second insulation film 16 is formed a conductor film having a predetermined thickness, e.g. the TiN/Al-Si/Ti/TiON/Ti lamination film 18 in which a Ti layer having a thickness of 5 to 70 nm or so, a TiON layer having a thickness 10 to 200 nm or so, a Ti layer having a thickness of 5 to 70 nm or so, a Al-Si layer having a thickness of 300 to 1500 nm or so, and a TiN layer having a thickness of 5 to 70 nm or so are piled in turn from below.

[0229] Additionally, in such a multi-layered structure, the uppermost TiN layer functions as an antireflection coating in the photolithographing step during fabrication process and as an antioxidation film of the Al-Si layer thereunder. The Al-Si layer functions as the principal part of the electrode requiring a conductive characteristic. The lower Ti/TiON/Ti lamination film functions as a barrier metal.

[0230] Again, in the TiN/Al-Si/Ti/TiON/Ti lamination film 18, its surface over the polysilicon dummy layer 14 with a thickness of 100 to 500 nm for making a level difference is higher than the surface of an area surrounded by the polysilicon dummy layer 14 by 100 to 500 nm or so.

[0231] Next, as shown in FIG. 24, using the CVD method for example, on the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is piled the dielectric film 20 made of Ta₂O₅, SiO₂, SiN or the like, in this embodiment Ta₂O₅ dielectric film 20 having a predetermined thickness of, e.g. 10 to 300 nm or so. Further, using the sputtering method for example, on the dielectric film is piled a conductor layer made of, e.g. a Ti layer, a TiN layer, or a Ti/TiN layered film having a predetermined thickness of, e.g. 20 to 500 nm or so.

[0232] Subsequently, via the photolithographing process and RIE process, these layered conductor layer and dielectric film are selectively removed by etching into a predetermined pattern.

[0233] In this way, on the TiN/Al-Si/Ti/TiON/Ti lamination film 18 in an area surrounded by the polysilicon dummy layer 14 for making a level difference, there is formed the upper electrode 22 made of a Ti layer, a TiN layer or a Ti/TiN layered film having a thickness of 20 to 500 nm or so through the dielectric film 20 having a thickness of 10 to 300 nm or so. The surface of upper electrode 22 is made equal to or higher than in level, the surface of lamination film 18 situated over the dummy layer 14.

[0234] Note that the surface of dielectric film 20 at this time is lower in level than the surface of lamination film 18 situated over the polysilicon dummy layer 14.

[0235] Next, as shown in FIG. 25, via the photolithographing process and RIE process, the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is selectively removed by etching into a predetermined pattern.

[0236] In this manner, the lower electrode 18 a made of the TiN/Al-Si/Ti/TiON/Ti lamination film having a recess form section in which the surface of its periphery over the polysilicon dummy layer 14 for making a level difference lies on a higher level than the surface of dielectric film 20 in its center having the upper electrode 22 formed thereon, is formed. Also, simultaneously with the formation of lower electrode 18 a, a lower layer wiring layer (not shown) made of a TiN/Al-Si/Ti/TiON/Ti lamination film of other element in LSI is formed.

[0237] The capacitance element comprised of the upper electrode 22 and lower electrode 18 a which sandwich the dielectric film 20 between them is thus formed.

[0238] Additionally, the surface of dielectric film 20 in the capacitance element at this time is lower in level than the surface of the periphery of lower electrode 18 a located over the polysilicon dummy layer 14.

[0239] Next, as shown in FIG. 26, the smoothing process to smooth unevenness of the whole surface of base body is carried out. Specifically, using the plasma CVD method for example, taking the TEOS as a raw material, on the whole surface of base body including the upper electrode 22 and lower electrode 18 a is piled, for example, a SiO₂ film up to a thickness of 300 to 1500 nm or so. Further, the SiO₂ film is coated with a SOG film. Thereafter, these SOG film and SiO₂ film are etched back.

[0240] In this way, the smoothing insulation film 24 which fills the recess of lower electrode 18 a with a recess form section and smooths the whole surface of base body is formed.

[0241] It is noted that, in the smoothing process of the whole surface of base body, i.e. the formation process of the smoothing insulation film 24, the surface of dielectric film 20 formed on the center of lower electrode 18 a with a recess form section is lower in level than the surface of the periphery of lower electrode 18 a with a recess form section located over the polysilicon dummy layer 14. Moreover, in a general smoothing etch-back, an etching rate of SiO₂ is not so different from that of Ti or TiN. Thus, when the SOG film and SiO₂ film are formed and then etched back, the surface of the periphery of lower electrode 18 a is exposed, but the surface of dielectric film 20 will never be exposed by etching. In other words, the periphery of lower electrode 18 a will serve as an etching stopper and so the dielectric film 20 under the upper electrode 22 will never sustain damage.

[0242] Next, as shown in FIG. 27, using the plasma CVD method for example, on the whole surface of base body including the periphery of lower electrode 18 a and the smoothing insulation film 24 is piled the insulation film 26 made of, e.g. a SiO₂ film. The smoothing insulation film 24 and insulation film 26 form the inter-layer insulation film 27 together.

[0243] Subsequently, using the photolithographing process and dry etching method, the inter-layer insulation film 27 on upper electrode 22 is selectively removed by etching and also the inter-layer insulation film 27 on the periphery of lower electrode 18 a is selectively removed etching for opening the first and second via-holes 28 a and 28 b. At this time, there may be a case where only the TiN layer on the surface of lower electrode 18 a is removed so as to reduce a contact resistance.

[0244] It is noted that, on this occasion, a film thickness of the inter-layer insulation film 27 on upper electrode 22 to be etched for opening the first via-hole 28 a is approximately equal to a film thickness of the inter-layer insulation film 27 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. For this reason, when these first and second via-holes 28 a and 28 b are opened, an excess over-etching to the surface of upper electrode 22 will never happen.

[0245] Next, as shown in FIG. 28, for example, an Al-alloy layer is piled using the sputtering method and then the Al-alloy layer is processed using the photolithographing process and dry etching method in order to form the first and second upper-layer wiring layers 30 a and 30 b made of the Al-alloy layer connected to the upper electrode 22 and the periphery of lower electrode 18 a through the first and second via-holes 28 a and 28 b.

[0246] Also, simultaneously with the formation of the first and second upper-layer wiring layers 30 a and 30 b, upper-layer wiring layers (not shown) of other element is LSI is formed.

[0247] As described above, in this embodiment, the polysilicon dummy layer 14 for making a level difference made of a polysilicon layer having a thickness of 100 to 500 nm or so is formed on the periphery of a predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12; the second insulation film 16 being formed on the whole surface of base body including the polysilicon dummy layer 14; the lower electrode 18 a with a recess form section in which the surface of its periphery lies on a higher level than the surface of its center being formed on the insulation film 16; the upper electrode 22 having a predetermined thickness of, e.g. 5 to 100 nm or so being formed on the center of lower electrode 18 a through the dielectric film 20 having a predetermined thickness of, e.g. 10 to 300 nm (that is, a dielectric film thinner than the dummy layer 14); and the surface of dielectric film 20 being made lower in level than the surface of the periphery of lower electrode 18 a located over the polysilicon dummy layer 14. Thus, after the SiO₂ film is piled on the whole surface of base body and further coated with the SOG film, when the smoothing process to etch back them is carried out, the periphery of lower electrode 18 a acts as an etching stopper and so the dielectric film 20 will never suffer damage due to etching. Therefore, it is possible to suppress the fluctuation in characteristics such as a capacitance value or the like and the deterioration of reliability on a capacitance element and thus obtain a capacitance element having satisfactory characteristics and a high reliability.

[0248] Moreover, when the first and second via-holes 28 a and 28 b are opened in order to form the first and second upper-layer wiring layers 30 a and 30 b which are connected to the upper electrode 22 and lower electrode 18 a, respectively, a film thickness of the inter-layer insulation film 27 on the upper electrode 22 to be etched for opening the first via-hole 28 a is approximately equal to a film thickness of the inter-layer insulation film 27 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. For this reason, an excess overetching to the surface of upper electrode 22 will never be performed and so the upper electrode 22 and Ta₂O₅ dielectric film 20 thereunder will never sustain damage. Therefore, it is possible to further suppress the fluctuation in characteristics such as a capacitance value or the like and the deterioration of reliability on a capacitance element and thus obtain a capacitance element having better characteristics and higher reliability.

[0249] Furthermore, in comparison between the first and second via-holes 28 a and 28 b, the depth of the second via-hole 28 b opened on the lower electrode 18 a is shallower than the depth of the first via-hole 28 a. Thus, of distances from the area where the upper electrode 22 and lower electrode 18 a are opposed and which functions effectively as a capacitance element, to the first and second upper-layer wiring layer 30 a and 30 b, a distance on the lower electrode side which generally tends to be longer than a distance on the upper electrode side is made shorter. Therefore, it is possible to reduce a difference in their impedances and suppress an increase of asymmetry in characteristics of a capacitance element. In other words, it is possible to improve symmetry in characteristics of a capacitance element.

[0250] (A Fifth Embodiment)

[0251]FIG. 29 is a schematic sectional diagram showing a capacitance element according to a fifth embodiment of the present invention. FIG. 30 and FIG. 31 are schematic sectional process diagrams for explaining a method of fabricating the capacitance element shown in FIG. 29. Additionally, the same elements as constituent elements of the capacitance element shown in FIG. 21 to FIG. 28 according to the fourth embodiment are denoted by the same reference numerals to omit at description thereof.

[0252] As shown in FIG. 29, the capacitance element according to this embodiment is characterized in that, instead of the polysilicon dummy layer 14 for making a level difference in the capacitance element shown in FIG. 20 according to the fourth embodiment, an insulation dummy layer made of SiN, SiO₂ and the like having a predetermined thickness, for example, a SiO₂ dummy layer 32 for making a level difference made of a SiO₂ layer having a thickness of 100 to 500 nm or so is formed. The other constituent elements are the same as those in the fourth embodiment.

[0253] Next, a method of fabricating the capacitance element shown in FIG. 29 with reference to schematic sectional process diagrams of FIG. 30 and FIG. 31.

[0254] To start with, as shown in FIG. 30, after the first insulation film 12 made of, e.g. a SiO₂ layer is formed on the semiconductor substrate 10, further on the first insulation film 12 is formed an insulation film, e.g. a SiO₂ film up to a thickness of 100 to 500 nm or so. Subsequently, by the photolithographing process and etching process, the SiO₂ film is selectively removed by etching into a predetermined pattern.

[0255] In this manner, the SiO₂ dummy layer 32 made of a SiO₂ film having a thickness of 100 to 500 nm or so is formed on the periphery of predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12.

[0256] Next, as shown in FIG. 31, in the same way as processes shown in FIG. 22 to FIG. 28 according to the fourth embodiment, the second insulation film 16 is formed on the whole surface of base body including the SiO₂ dummy layer 32; the TiN/Al-Si/Ti/TiON/Ti lamination film 18 being formed on the second insulation film 16; the upper electrode 22 being formed on the TiN/Al-Si/Ti/TiON/Ti lamination film 18 through the dielectric film 20; and the TiN/Al-Si/Ti/TiON/Ti lamination film 18 being patterned by the photolithographing process and RIE process to form the lower electrode 18 a having a recess form section in which the surface of its periphery situated over the SiO₂ dummy layer 32 lies on a higher level than the surface of its center on which the upper electrode 22 is formed.

[0257] In this way, the capacitance element comprised of the upper electrode 22 and lower electrode 18 a which sandwich the dielectric film 20 between them is formed.

[0258] Note that the surface of dielectric film 20 in the capacitance element at this moment is lower in level than the surface of the periphery of lower electrode 18 a situated over the SiO₂ dummy layer 32.

[0259] Subsequently, on the whole surface of base body including the upper electrode 22 and lower electrode 18 a is piled a SiO₂ film which is further coated with a SOG film. Thereafter, these SOG film and SiO₂ film are etched back for smoothing them to fill the recess of lower electrode 18 a with a recess form section and also cover the surface of upper electrode 22. The smoothing insulation film 24 that smooths the whole surface of base body is thus formed.

[0260] It is noted that, in the smoothing process of the whole surface of base body, i.e. the forming process of the smoothing insulation film 24, the surface of dielectric film 20 formed on the center of lower electrode 18 a with a recess form section is lower in level than the surface of the periphery of lower electrode 18 a situated over the SiO₂ dummy layer 32. Under a general smoothing etch-back condition, the difference between etching rates of SiO₂ and Ti or TiN is not so large. For this reason, when the SOG film and SiO₂ film are etched back, the periphery of lower electrode 18 a acts as an etching stopper. Thus, although the surface of the periphery of lower electrode 18 a may be exposed, the surface of dielectric film 20 will never be exposed by etching.

[0261] Subsequently, on the whole surface of base body including the periphery of lower electrode 18 a and the smoothing insulation film 24 is piled the insulation film 26 made of, e.g. a SiO₂ film to form the inter-layer insulation film 27 made of the smoothing insulation film 24 and insulation film 26. Then, the inter-layer insulation film 27 on upper electrode 22 is selectively removed by etching and also the inter-layer insulation film 27 on the periphery of lower electrode 18 a is selectively removed by etching to open the first and second via-holes 28 a and 28 b. There may be a case where the TiN layer of the surface of lower electrode 18 a is removed.

[0262] Additionally, at this time, a film thickness of the inter-layer insulation film 27 on upper electrode 22 to be etched for opening the first via-hole 28 a is approximately equal to a film thickness of the inter-layer insulation film 26 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. Therefore, when these first and second via-holes 28 a and 28 b are opened, an excess overetching to the surface of upper electrode 22 will never happen.

[0263] Subsequently, the first and second upper-layer wiring layers 30 a and 30 b which are respectively connected to the upper electrode 22 and the periphery of lower electrode 18 a through the first and second via-holes 28 a and 28 b are formed.

[0264] As described above, in this embodiment, the SiO₂ dummy layer 32 having a predetermined thickness of, e.g. 100 to 500 nm or so for making a level difference is formed on the periphery of predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12; the second insulation film 16 being formed on the whole surface of base body including the SiO₂ dummy layer 32; the lower electrode 18 a having a recess form section in which the surface of its periphery over the SiO₂ dummy layer 32 lies on a higher level than the surface of its center being formed; and the upper electrode 22 being formed on the center through the dielectric film 20 having the surface which is lower than the surface of the periphery of lower electrode 18 a over the SiO₂ dummy layer 32. Therefore, when the SiO₂ film is piled on the whole surface of base body, further coated with SOG film and then processed to be smoothed by etching back, the periphery of lower electrode 18 a acts as an etching stopper and so the dielectric film 20 will never sustain damage by etching. Consequently, similarly to the first embodiment, it is possible to suppress the fluctuation in characteristics such as a capacitance value or the like and the degradation of reliability on a capacitance element, thus allowing a capacitance element having satisfactory characteristics and high reliability to be obtained.

[0265] Moreover, when the first and second via-holes 28 a and 28 b are opened in order to form the first and second upper-layer wiring layers 30 a and 30 b which are respectively connected to the upper electrode 22 and lower electrode 18 a of the capacitance element a film thickness of the inter-layer insulation film 27 on upper electrode 22 to be etched for opening the first via-hole 28 a is nearly equal to a film thickness of the inter-layer insulation film 27 on the periphery of lower electrode 18 a to be etched for opening the second via-hole 28 b. For this reason, an excess overetching to the surface of upper electrode 22 will never take place and so the upper electrode 22 and the dielectric film 20 thereunder will never suffer damage. Therefore, just as in the first embodiment, it is possible to further suppress the fluctuation in characteristics such as a capacitance value or the like and the deterioration of reliability on a capacitance element thereby allowing a capacitance element having better characteristics and a higher reliability to be obtained.

[0266] Furthermore, the depth of the second via-hole 28 b opened on the lower electrode 18 a is approximately equal to the depth of the first via-hole 28 a opened on the upper electrode 22. Thus, of distances from the area where the upper electrode 22 and lower electrode 18 a are opposed and which functions effectively as a capacitance element to the first and second upper-layer wiring layers 30 a and 30 b, a distance on the lower electrode side which generally tends to be longer than that on the upper electrode side is made shorter. Therefore, similarly to the first embodiment, it is possible to reduce the difference between their impedances and suppress an increase of asymmetry in characteristics of a capacitance element, thus enabling symmetry in characteristics of a capacitance element to be improved.

[0267] Additionally, the above described fifth embodiment has the SiO₂ dummy layer 32 having a predetermined thickness of, e.g. 100 to 500 nm or so for making a level difference formed on the periphery of predefined area of forming a capacitance element on the semiconductor substrate 10 through the first insulation film 12.

[0268] However, instead of forming such a SiO₂ dummy layer 32, the first insulation layer 12 in the center of a predefined area of forming a capacitance element on the semiconductor substrate 10 may selectively be removed by etching through the photolithographing process and etching process to form a recess about 100 to 500 nm deep. In addition, the selective etching of the first insulation layer 12 may be combined with the dummy layer 32(or dummy layer 14 or dummy layer 34 described below to form a final dummy layer, whereby the recess about 100 to 500 nm in depth can also be formed.

[0269] In any of these cases, it will be possible to form the second insulation film 16 on the first insulation film 12 in which the recess about 100 to 500 nm deep is formed in the center of the predefined area of forming the capacitance element, in the same way as in the second embodiment; form the TiN/Al-Si/Ti/TiON/Ti lamination film 18 on the second insulation film 16; and pattern the TiN/Al-Si/Ti/TiON/Ti lamination film 18 to form the lower electrode 18 a having a recess form section in which the surface of its periphery lies on a higher level than the surface of its center located above the recess formed on the first insulation film 12. Therefore, the same effect as in the above fifth embodiment can be achieved.

[0270] (A Sixth Embodiment)

[0271]FIG. 32 is a schematic sectional diagram showing a capacitance element according to a sixth embodiment of the present invention. FIG. 33 to FIG. 38 are each a schematic sectional process diagram for explaining a method of fabricating the capacitance element shown in FIG. 32. It is noted herein that the same elements as constituent elements of the capacitance element shown in FIG. 20 to FIG. 28 according to the fourth embodiment are denoted by the same reference numerals to omit a description thereof.

[0272] As shown in FIG. 32, the capacitance element according to this embodiment is characterized in that, as compared with the capacitance element shown in FIG. 20 according to the fourth embodiment, instead of the polysilicon dummy layer 14 formed on the periphery of the capacitance element for making a level difference a polysilicon dummy layer 34 having the same thickness of, e.g. 100 to 500 nm or so for making a level difference is formed on the periphery of the capacitance element.

[0273] Moreover, it is also characterized in that, instead of the lower electrode 18 a made of, e.g. TiN/Al-Si/Ti/TiON/Ti and having a recess form section shown in FIG. 20 according to the fourth embodiment, a flat lower electrode 18 b made of, e.g. TiN/Al-Si/Ti/TiON/Ti is formed and also, separately from the lower electrode 18 b, a dummy electrode 18 c made of, e.g. TiN/Al-Si/Ti/TiON/Ti having a higher surface than that of the upper electrode 22 is formed over the polysilicon dummy layer 34 for making a level difference surrounding the capacitance element.

[0274] The other components are approximately the same as those of the fourth embodiment.

[0275] Next, a method of fabricating the capacitance element shown in FIG. 32 will be described with reference to schematic sectional process diagrams of FIG. 32 to FIG. 38.

[0276] To begin with, as shown in FIG. 33, after the first insulation film 12 made of, e.g. a SiO₂ film is formed on the semiconductor substrate 10, a polysilicon layer is formed further on the first insulation film 12 up to a predetermined thickness of, e.g. 100 to 500 nm or so.

[0277] Subsequently, through the photolithographing process and RIE process, the polysilicon layer is selectively removed by etching into a predetermined pattern.

[0278] In this way, a polysilicon dummy layer 34 made of a polysilicon layer having a thickness of 100 to 500 nm or so for making a level difference is formed on the periphery of a predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12.

[0279] Additionally, the forming process of the polysilicon dummy layer 34 can be combined with a forming process of a polysilicon layer used as a gate electrode of the other element, e.g. MOSTr, a resistance layer of a resistance element or an electrode of BipTr in LSI.

[0280] Next, as shown in FIG. 34, in the same way as processes shown in FIG. 22 to FIG. 24 according to the fourth embodiment, the second insulation film 16 is formed on the whole surface of base body including the polysilicon dummy layer 34 for making a level difference. This insulation film 16 can be dispensed with. Then, on the second insulation film 16 is formed a TiN/Al-Si/Ti/TiON/Ti lamination film or a layered film of Cu, Al-Cu and the like, in this embodiment a TiN/Al-Si/Ti/TiON/Ti lamination film 18. On this TiN/Al-Si/Ti/TiON/Ti lamination film 18 is formed an upper electrode 22 made of a Ti film, a TiN film or a Ti/TiN layered film through a dielectric film 20 of Ta₂O₅, SiO₂, SiN or the like, in this embodiment Ta₂O₅.

[0281] Note that the surface of the dielectric film 20 at this moment is lower in height than the top surface of the TiN/Al-Si/Ti/TiON/Ti lamination film 18 located over the polysilicon dummy layer 34.

[0282] Next, as shown in FIG. 35, through the photolithographing process and RIE process, the TiN/Al-Si/Ti/TiON/Ti lamination film 18 is selectively removed by etching into a predetermined pattern.

[0283] In this manner, the lower electrode 18 b made of TiN/Al-Si/Ti/TiON/Ti is formed in the predefined area of forming the capacitance element on the second insulation film 16 and also, separately from the lower electrode 18 b, the dummy electrode 18 c of TiN/Al-Si/Ti/TiON/Ti having the top surface higher than the surface of lower electrode 18 b is formed over the polysilicon dummy layer 34 surrounding the predefined area of forming the capacitance element.

[0284] Simultaneously with the formation of lower electrode 18 b, lower-layer wiring layers (not shown) made of a TiN/Al-Si/Ti/TiON/Ti lamination film of other elements in LSI are formed.

[0285] The capacitance element is thus formed, which is comprised of the upper electrode 22 and lower electrode 18 b sandwiching the dielectric film 20 between them.

[0286] Note that the surface of the dielectric film 20 at this time is lower in height than the top surface of the dummy electrode 18 c surrounding the predefined area of forming the capacitance element and located over the polysilicon dummy layer 34.

[0287] Next, as shown in FIG. 36, on the whole surface of base body including the upper electrode 22 and lower electrode 18 b is piled a SiO₂ film up to a thickness of 300 to 1500 nm or so. This SiO₂ film is further coated with a SOG film. Thereafter, there SOG film and SiO₂ film are processed to be smoothed by etching back.

[0288] In this way, the recess surrounded by the dummy electrode 18 c is filled and smoothed to form the smoothing insulation film 24.

[0289] In this process of smoothing the whole surface of base body, namely, the process of forming the smoothing insulation film 24, the surface of dielectric film 20 formed on the lower electrode 18 b is lower in level than the top surface of dummy electrode 18 c surrounding the predefined area of forming the capacitance element and located over the polysilicon dummy layer 34, Under a normal etch-back condition, there is not a large difference between an etching rate of Ti or TiN and that of SiO₂. Thus, when the SOG film and SiO₂ film are etched back, the surface of dielectric film 20 will never be exposed by etching.

[0290] Next, as shown in FIG. 37, using the plasma CVD method for example, on the whole surface of base body including the dummy electrode 18 c and smoothing insulation film 24 is piled the insulation film 26. The smoothing insulation film 24 and insulation film 26 make the inter-layer insulation film 27 together.

[0291] Subsequently, using the photolithographing process and dry etching method, the inter-layer insulation film 27 on the upper electrode 22 and lower electrode 18 b is selectively removed by etching to open the first and second via-holes 28 a and 28 b.

[0292] Next, as shown in FIG. 38, after an Al-alloy layer is piled using the sputtering method for example the Al-alloy layer is processed using the photolithographing process and dry etching method to form the first and second upper-layer wiring layers 30 a and 30 c made of Al-alloy layer and each connected to the upper electrode 22 and the periphery of lower electrode 18 b through the first and second via-holes 28 a and 28 c.

[0293] Simultaneously with the formation of the first and second upper-layer wiring layers 30 a and 30 c, upper layer wiring layers (not shown) of other elements in LSI are formed.

[0294] As described above, in this embodiment, the polysilicon dummy layer 34 having a thickness of about 100 to 500 nm for making a level difference is formed on the periphery of a predefined area of forming the capacitance element on the semiconductor substrate 10 through the first insulation film 12; the lamination film 18 of, e.g. TiN/Al-Si/Ti/TiON/Ti being formed on the whole surface of base body including the polysilicon dummy layer 34 through the second insulation film 16 and patterned into a predetermined shape; the lower electrode 18 b of TiN/Al-Si/Ti/TiON/Ti being formed in the predefined area of forming the capacitance element; the dummy electrode 18 c of TiN/Al-Si/Ti/TiON/Ti having the surface higher than the surface of lower electrode 18 b being formed above the polysilicon dummy layer 34 surrounding the lower electrode 18 b; the upper electrode 22 being formed on the lower electrode 18 b through the dielectric film 20; and the surface of dielectric film 20 is made lower in height than the top surface of dummy electrode 18 c formed above the polysilicon dummy layer 34. Thus, when the smoothing process is performed by etching back after a SiO₂ film is piled on the whole surface of base body and further coated with a SOG film, the dummy electrode 18 c acts as an etching stopper and so the dielectric film 20 under the upper electrode 22 will never sustain damage by etching. Therefore, similarly to the fourth embodiment, it is possible to suppress the fluctuation in characteristics, such as a capacitance value or the like and the deterioration of reliability on a capacitance element, thereby allowing a capacitance element having satisfactory characteristics and high reliability to be obtained.

[0295] Additionally, in the fourth to sixth embodiments, there is described the case where the lower electrode 18 a or 18 b is connected to the second upper-layer wiring layer 30 b or 30 c through the second via-hole 28 b or 28 c. However, there may be a case where the lower electrode 18 a or 18 b also serves as a wiring layer intactly and is connected to another element of LSI.

[0296] In this case, it is unnecessary to selectively remove the inter-layer insulation film 27 on the lower electrode 18 a or 18 b by etching so as to open the second via-hole 28 b or 28 c.

[0297] Moreover, in order to form the first and second upper-layer wiring layers 30 a, 30 b and 30 c, the following method can be employed instead of piling the Al-alloy layer and processing the same. After a W(tungsten) layer is piled using the CVD method, W plugs which respectively fill the first and second via-holes 28 a, 28 b and 28 c are formed by etching back. Further, using the sputtering method is piled an Al-alloy layer. Thereafter, the Al-alloy layer is processed to form the first and second upper-layer wiring layers which are connected to the W plugs inside the first and second via-holes 28 a 28 b and 28 c, respectively. 

1. A semiconductor device characterized by comprising: a lower electrode that is formed on a semiconductor substrate through a first insulation film and has a recess form section in which the surface of its periphery lies on a higher level than the surface of its center; an upper electrode that is formed on the center of the lower electrode through a dielectric film, the surface of which lies on a lower level than the surface of the periphery of the lower electrode; and a second insulation film that fills a recess of the lower electrode having the recess form section.
 2. A semiconductor device according to claim 1, characterized in that: a third insulation film is formed on the periphery of the lower electrode, the upper electrode and the second insulation film to make an inter-layer insulation film; a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film; and a second wiring layer that is connected to the periphery of the lower electrode through a second via-hole opened in the inter-layer insulation film.
 3. A semiconductor device according to claim 1, characterized in that a dummy layer provided below the periphery of the lower electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 4. A semiconductor device according to claim 2, characterized in that a dummy layer provided below the periphery of the lower electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 5. A semiconductor device characterized by comprising: a lower electrode formed on a semiconductor substrate through a first insulation film; a dummy electrode having the surface higher than the surface of the lower electrode; an upper electrode formed on the lower electrode through a dielectric film, the surface of which lies on a level lower than the top surface of the dummy electrode; and a second insulation film that fills a recess surrounded by the dummy electrode.
 6. A semiconductor device according to claim 5, characterized in that: a third insulation film is formed on the dummy electrode, the upper electrode and the second insulation film to make an inter-layer insulation film; a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film; and a second wiring layer that is connected to the lower electrode through a second via-hole opened in the inter-layer insulation film.
 7. A semiconductor device according to claim 5, characterized in that a dummy layer provided below the dummy electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 8. A semiconductor device according to claim 5, characterized in that a dummy layer provided below the dummy electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 9. A semiconductor device characterized by comprising: a lower electrode that is formed on a semiconductor substrate through a first insulation film and has a recess form section in which the surface of its periphery lies on a level higher than the surface of its center; an upper electrode that is formed on the center of the lower electrode through a dielectric film and has the surface lower in level than the surface of the periphery of the lower electrode; and a second insulation film that fills a recess of the lower electrode having a recess form section and also covers the surface of the upper electrode.
 10. A semiconductor device according to claim 9, characterized in that: a third insulation film is formed on the periphery of the lower electrode and the second insulation film to make an inter-layer insulation film; a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film; and a second wiring layer that is connected to the periphery of the lower electrode through a second via-hole opened in the inter-layer insulation film.
 11. A semiconductor device according to claim 9, characterized in that a dummy layer provided below the periphery of the lower electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 12. A semiconductor device according to claim 10, characterized in that a dummy layer provided below the periphery of the lower electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 13. A semiconductor device characterized by comprising: a lower electrode formed on a semiconductor substrate through a first insulation film; a dummy electrode that is formed on the periphery of the lower electrode and has the surface higher in level than the surface of the lower electrode; an upper electrode that is formed on the lower electrode through a dielectric film and has the surface lower in level than the top surface of the dummy electrode; and a second insulation film that fills a recess surrounded by the dummy electrode and also covers the surface of the lower electrode and upper electrode.
 14. A semiconductor device according to claim 13, characterized in that: a third insulation film is formed on the dummy electrode, the upper electrode and the second insulation film to make an inter-layer insulation film; a first wiring layer that is connected to the upper electrode through a first via-hole opened in the inter-layer insulation film; and a second wiring layer that is connected to the lower electrode through a second via-hole opened in the inter-layer insulation film.
 15. A semiconductor device according to claim 13, characterized in that the dummy layer provided below the dummy electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 16. A semiconductor device according to claim 14, characterized in that the dummy layer provided below the dummy electrode for making a level difference is formed out of a layer of the same material as that of an electrode or a resistance layer of another element.
 17. A method of fabricating a semiconductor device characterized by comprising the steps of: forming a dummy layer having a predetermined thickness for making a level difference on the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; forming a lower electrode that has a recess form section in which the surface of its periphery lies on a level higher than the surface of its center, on the predefined area of forming the capacitance element, by piling a conductor film on the first insulation film and the dummy layer and then patterning the conductor film; forming an upper electrode on the center of the lower electrode through a dielectric film, the surface of which lies on a level lower than the surface of the periphery of the lower electrode; and forming a second insulation film on the whole surface of a base body to fill a recess of the lower electrode having the recess form section.
 18. A method of fabricating a semiconductor device according to claim 17, characterized by further comprising the steps of: forming a third insulation film on the whole surface of the base body including the periphery of the lower electrode, the upper electrode and the second insulation film to make an inter-layer insulation film; opening a first via-hole in the inter-layer insulation film on the upper electrode and also opening a second via-hole in the inter-layer insulation film on the periphery of the lower electrode; and forming a first wiring layer that is connected to the upper electrode through the first via-hole and also forming a second wiring layer that is connected to the periphery of the lower electrode through the second via-hole.
 19. A method of fabricating a semiconductor device according to claim 17, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element.
 20. A method of fabricating a semiconductor device according to claim 18, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element.
 21. A method of fabricating a semiconductor device characterized by comprising the steps of: forming a dummy layer having a predetermined thickness for making a level difference, around a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; forming a lower electrode in the predefined area of forming a capacitance element by piling a conductor film on the first insulation film and the dummy layer, thereafter patterning the conductor film, and also forming a dummy electrode that covers the dummy layer and has the surface higher than the surface of the lower electrode, around the predefined area of forming a capacitance element; forming an upper electrode on the lower electrode through a dielectric film, the surface of which lies on a level lower than the top surface of the dummy electrode; and forming a second insulation film on the whole surface of a base body to fill a recess surrounded by the dummy electrode.
 22. A method of fabricating a semiconductor device according to claim 21, characterized by further comprising the steps of: forming a third insulation film on the whole surface of the base body including the dummy electrode, the upper electrode and the second insulation film to make an inter-layer insulation film; opening a first via-hole in the inter-layer insulation film on the upper electrode and also opening a second via-hole in the inter-layer insulation film on the lower electrode; and forming a first wiring layer that is connected to the upper electrode through the first via-hole and also forming a second wiring layer that is connected to the lower electrode through the second via-hole.
 23. A method of fabricating a semiconductor device according to claim 21, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element.
 24. A method of fabricating a semiconductor device according to claim 22, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element.
 25. A method of fabricating a semiconductor device characterized by comprising the steps of: forming a dummy layer having a predetermined thickness for making a level difference on the periphery of a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; forming a lower electrode having a recess form section in which the surface of its periphery lies on a level higher than the surface of its center, in a predefined area of forming a capacitance element, by piling a conductor film on the first insulation film and the dummy layer and then patterning the conductor film; foaming an upper electrode, the surface of which lies on a level lower than the surface of the periphery of the lower electrode, on the center of the lower electrode through a dielectric film; and forming a second insulation film on the whole surface of a base body to fill a recess of the lower electrode having a recess form section and also cover the surface of the upper electrode.
 26. A method of fabricating a semiconductor device according to claim 25, characterized by further comprising the steps of: forming a third insulation film on the whole surface of the base body including the periphery of the lower electrode and the second insulation film to make an inter-layer insulation film; opening a first via-hole in the inter layer insulation film on the upper electrode and also opening a second via-hole in the inter-layer insulation film on the periphery of the lower electrode; and forming a first wiring layer that is connected to the upper electrode through the first via-hole and also forming a second wiring layer that is connected to the periphery of the lower electrode through the second via-hole.
 27. A method of fabricating a semiconductor device according to claim 25, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element.
 28. A method of fabricating a semiconductor device according to claim 26, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element.
 29. A method of fabricating a semiconductor device characterized by comprising the steps of: forming a dummy layer having a predetermined thickness for making a level difference around a predefined area of forming a capacitance element on a semiconductor substrate through a first insulation film; forming a lower electrode in the predefined area of forming a capacitance element by piling a conductor film on the first insulation film and the dummy layer, thereafter patterning the conductor film, and also forming a dummy electrode that covers the dummy layer and has the surface higher than the surface of the lower electrode, around the predefined area of forming a capacitance element; forming an upper electrode, the surface of which lies on a level lower than the top surface of the dummy electrode, on the lower electrode through a dielectric film; and forming a second insulation film on the whole surface of a base body to fill a recess surrounded by the dummy electrode and also cover the surface of the lower electrode and upper electrode.
 30. A method of fabricating a semiconductor device according to claim 29, characterized by further comprising the steps of: forming a third insulation film on the whole surface of the base body including the dummy electrode and the second insulation film to make an inter-layer insulation film opening a first via-hole in the inter-layer insulation film on the upper electrode and also opening a second via-hole in the inter-layer insulation film on the lower electrode; and forming a first wiring layer that is connected to the upper electrode through the first via-hole and also forming a second wiring layer that is connected to the lower electrode through the second via-hole.
 31. A method of fabricating a semiconductor device according to claim 29, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of an electrode and a resistance layer of another element.
 32. A method of fabricating a semiconductor device according to claim 30, characterized in that the step of forming the dummy layer for making a level difference is combined with a step of forming an electrode or a resistance layer of another element. 